Abstract
Due to their responsiveness to modulation by external direct current fields, dielectric tunable materials are extensively utilized in integrated components, such as ferroelectric phase shifters. Barium strontium titanate ceramics have been considered the most potential tunable materials for a long time. However, the significant dielectric loss and high voltage drive have limited their further applications. Recently, Bi6Ti5WO22 ceramic has regained attention for its high dielectric tunability with low loss. In this study, we judiciously introduce Nb5+ with a larger ionic radius, replacing Ti4+ and W6+. This successful substitution enables the modulation of the phase transition temperature of Bi6Ti5WO22 ceramics to room temperature, resulting in superior tunable properties. Specifically, the 0.7Bi6Ti5WO22−0.3Bi6Ti4Nb2O22 ceramics exhibit giant tunability (~75.6%) with ultralow loss (<0.002) under a low electric field (1.5 kV/mm). This tunability is twice that of barium strontium titanate ceramics with a similar dielectric constant and only one-tenth of the loss. Neutron powder diffraction and transmission-electron-microscopy illustrate the nanodomains and micro-strains influenced by ion substitution. Density functional theory simulation calculations reveal the contribution of ion substitution to polarization. The research provides an ideal substitute for tunable material and a general strategy for adjusting phase transition temperature to improve dielectric properties.
Similar content being viewed by others
Introduction
Capacitors constitute the fundamental components of microwave-integrated devices within electronic systems, and their performance is primarily governed by the dielectric materials employed. Dielectric tunable materials are materials whose dielectric constant can be modulated by an external direct current field (E). Due to their widespread application in devices such as microwave phase shifters and phased-array radars, dielectric tunable materials have attracted extensive research interest1,2,3,4,5,6. A standard parameter for evaluating the tunable performance of materials is dielectric tunability (T), which represents the maximum nonlinearity of reversible dielectric constants1:
where εr(0) is the dielectric constant of the material without external direct current bias, and εr(E) is the dielectric constant under an applied direct current bias electric field (E).
In general, the dielectric tunability of materials is positively correlated with the strength of the applied electric field. In current research, the pursuit of higher T often overlooks the applied electric field intensity. Methods such as manufacturing thin films are employed to significantly increase the intrinsic breakdown strength of materials, achieving higher tunability by applying high electric fields. However, this approach contradicts the practical requirement for lower bias voltage in real applications. Addressing this situation, Hu et al. introduced the concept of effective tunability Te7:
where T is the dielectric tunability at a specific applied electric bias, and E is a specific applied electric bias (E ≥ 0.5 kV/mm).
Barium strontium titanate ceramic ((Ba, Sr)TiO3, abbreviated as BST) has been considered the most potential tunable material for a long time. In the BST solid solution series, Ba0.65Sr0.35TiO3 (abbreviated as BST65) exhibits the highest effective tunability at room temperature, ranging from 0.15 to 0.47,8,9,10. Such effective tunability meets practical requirements, but the large dielectric constant and high loss limit its further applications. The incorporation of organic compounds can reduce the dielectric constant of the material7,11,12,13,14,15,16. The introduction of the ferroelectric phase can reduce the dielectric loss of BST ceramics17,18,19,20,21. However, both methods inevitably lead to a decrease in the effective tunability of the material. Despite extensive research in these two directions, breakthrough progress has yet to be achieved. Over time, many new tunable ceramic systems have been discovered and studied. These include ferroelectric materials such as Pb(Zr, Ti)O3, (Bi, Na)TiO3, (Na, K)NbO3, Ag(Ta, Nb)O3, as well as some non-ferroelectric materials like (Bi, Zn, Nb)O722,23,24,25,26,27,28,29,30. However, these materials have not been able to successfully replace the BST ceramic system in the tunable field because of their inferior effective tunability compared to BST65. In summary, the insufficient effective tunability and high loss impede further research on tunable materials, thereby restricting the potential applications of both tunable materials and devices.
Results
Bi6Ti5WO22 ceramic (abbreviated as BTW) has recently regained attention for its high dielectric tunability with low loss in our previous work31,32. We detailed the preparation and structural characterization of dense and phase-pure BTW ceramic, showcasing a remarkable 40% tunability at 3 kV/mm32. The utilization of ion substitution to achieve solid solution ceramics has proven to be an effective strategy for enhancing dielectric performance33. Experimental evidence suggests that optimal effective tunability is typically achieved near the intermediate temperature (abbreviated as Tm), which is the reason why BST65 with a Tm of approximately 20 °C has the highest tunability among solid solution ceramics. Since Tm of BTW is approximately 10 °C, achieving better tunable performance requires shifting its Tm toward higher values. Based on our previous studies on the structure of pure BTW, the main source of material polarization is the relative displacement of the Ti-O octahedra at the two Ti4+/W6+ shared sites32. Therefore, we believe that ion substitution at these positions can effectively tune the material’s properties. Considering that the radius of Ti4+ ions is 0.605 Å and that of W6+ ions is 0.60 Å, we consider Nb5+ ions with a radius of 0.64 Å to be a promising choice34. On the one hand, the relatively close ion radius allows Nb5+ ions to bind to the existing lattice framework to form a solid solution without generating a second phase; on the other hand, the slightly larger ion radius enables the introduction of Nb5+ ions to induce a change in lattice constant, thereby adjusting the phase transition temperature and affecting the dielectric properties. Additionally, the pentavalent state of Nb5+ ions ensures that the structural charge balance is maintained when two Nb5+ ions replace one W6+ and one Ti4+ ion. Building upon this idea, we judiciously designed a series of (1-x)Bi6Ti5WO22−xBi6Ti4Nb2O22 (0 ≤ x ≤ 0.6) solid solution ceramics (abbreviated as BTW-BTN).
Figure 1d illustrates the X-ray diffraction (XRD) patterns of the solid solution ceramics. It can be observed that for x ≤ 0.5, the XRD diffraction peaks match the characteristic pnn2 peaks of BTW. No distinct secondary phase peaks are evident, even for the composition until x = 0.5. However, a considerable presence of the secondary phase, Bi6Ti3WO18, is observed for x = 0.6. This indicates that the maximum solid solubility of BTW-BTN is approximately 50%, a fact corroborated by scanning electron microscope (SEM) micrographs (Fig. 1e). With the Nb content increases, the grain size of the samples progressively increases, which is caused by the slight increase in sintering temperature with the introduction of Nb. However, up to x = 0.4, the surface grains of the samples are very uniform, with no presence of any secondary phase. Thin-plate-shaped secondary phases become noticeable starting from x = 0.5 and are even more pronounced at x = 0.6. Energy dispersive X-ray spectrometry (EDS) analysis (Supplementary Fig. 1) confirms that these plate-like secondary phases are enriched in Bi. Combining SEM micrographs, EDS elemental analysis, and characteristic peaks in XRD, we preliminarily infer that the impurity phases are probable to be Bi6Ti3WO18 and Bi3TiNbO9, which are considered to be iso-structural35. Moreover, the refined results of the room-temperature XRD patterns indicate that, with the increasing Nb content, the main XRD peak shifts to lower angles, indicating an enlargement of lattice constants due to the successful introduction of Nb (as depicted in Fig. 1d), with detailed XRD refinement results are shown in Supplementary Fig. 2. The theoretical density of the solid solution material was computed based on the refinement results. Through comparison with experimentally measured density, it was established that the relative densities of ceramics with compositions ranging from x = 0.1 to 0.4 consistently exceed 97% (Supplementary Fig. 3).
To comprehensively understand the impact of Nb incorporation on the dielectric performance of BTW-BTN, the temperature-dependent dielectric spectra were measured (Fig. 2a). With the increasing Nb5+ content, the phase transition temperature of BTW-BTN shifts towards higher temperatures, leading to the successful generation of a series of solid solution ceramics with continuous variations in phase transition temperatures. For compositions with x = 0.2, 0.3, and 0.4, the peak dielectric constants experience a remarkable increase, reaching levels as high as ~11000. Supplementary Fig. 4 presents detailed temperature-dependent dielectric spectra for each component. The alteration of dielectric loss adheres to the general trend observed in composite ferroelectric ceramics: a peak near Tm is followed by a decrease in loss beyond Tm, maintaining them at very low levels. Figure 2b depicts the relationship between Tm and the content of Nb. The conductivity exhibits a similar pattern in its temperature-dependent spectra, showing a distinct transition near Tm (Supplementary Fig. 5). Notably, Tm exhibits almost linear variation with the introduction of Nb. Specifically, for compositions with x = 0.3 and 0.4, the phase transition temperatures are around 15 °C and 25 °C, respectively, close to room temperature. This suggests that the high dielectric constants and strong polarization in the vicinity of Tm can be effectively harnessed, leading to elevated tunability.
The relaxation behaviors of BTW-BTN ceramics with different Nb5+ contents exhibit some variations across frequencies. The activation energy for dielectric relaxation loss in BTW-BTN ceramics was calculated, and the relationship between ln f and 1000/T for BTW-BTN ceramics with various Nb5+ contents is presented in Fig. 2c. The activation energy can be determined from the slope using the following formula36:
where f is the measured frequency value, T represents the inflection point temperature of loss for each composition at different frequencies, and kB is the Boltzmann constant. Although this formula yields activation energies with some error, it qualitatively allows for comparing relaxation energy strengths among different compositions. From the graph, it can be observed that the slope increases with higher Nb5+ content. This behavior arises due to the enlargement of grain size upon Nb5+ introduction, which results in an increase in both grain boundary charges and space charges within the ceramic. Under the influence of an external electric field, the transfer and reorientation of free charges become more challenging, consequently increasing activation energy. This enhanced energy can be partly characterized through atomic force microscopy (AFM) imaging. Figure 2e illustrates AFM images of the induced compressive stress for different compositions at room temperature. Supplementary Fig. 6 displays the surface morphology of the three samples, which appear sufficiently smooth. The upper images show amplitude images captured immediately after applying a reverse voltage to a portion of the sample surface, while the lower images are captured from the same location after 20 minutes. The disparity between the two sets of images reflects the duration of the polarization process. Notably, in the case of the x = 0.1 composition, there is almost no amplitude remaining in the image taken after 20 minutes, whereas for the x = 0.4 composition, the difference between the images captured after 20 minutes and immediately after applying the voltage is minimal. The behavior of the x = 0.3 composition falls between these two extremes. The situation of phase behavior shows a similar trend (Supplementary Fig. 7). This indicates that with the introduction of Nb5+, the polarization of the sample at room temperature becomes more challenging, resulting in poorer relaxation behavior. In ferroelectric materials, such behavior is often attributed to changes in domain structures, which will be discussed in detail in the subsequent sections.
The measurement of ferroelectric properties was also successfully conducted. Figure 2d illustrates the polarization-electric field hysteresis loops (P-E loops) and strain coefficients for different solid solution ceramics. The P-E loops of x = 0.3 and x = 0.5 overlap, making them difficult to distinguish. The curves for each component separately plotted can be found in Supplementary Fig. 12. As Nb5+ content increases, the polarization at the same field strength weakens, and the P-E loops exhibit more characteristic ferroelectric behavior. This phenomenon can be easily understood as the Tm shifts towards room temperature. Notably, BTW-BTN exhibits significant uniaxial strain, with considerable strain (0.1% to 0.2%) even at low electric fields of 80 kV/cm. Compositions x = 0.2 and x = 0.3 both demonstrate strain strengths of nearly 0.2%, which is quite remarkable for lead-free perovskite ceramics. The curves of different components under breakdown field strength are shown in Supplementary Fig. 8. Figure 2f compiles temperature-dependent P-E loops for different solid solution compositions. Each composition was tested at intervals of 10 °C from 30 °C to 100 °C, resulting in eight P-E loops. Different colors represent the degree of curve in the loops, indicative of the strength of the ferroelectric behavior (red lines are more linear, while blue lines are more curved). This set of temperature-dependent P-E loops reveals a strong regularity, as the Tm shifts towards higher temperatures with increasing Nb5+ content. Moreover, the temperature at which the P-E loops tend towards linearity also shifts towards higher temperatures, demonstrating a close alignment with the dielectric performance.
Figure 3a illustrates the dielectric tunability performance of BTW-BTN ceramics measured at room temperature under 10 kHz. The response of the dielectric constant and dielectric loss of different components to the electric field is shown in Supplementary Fig. 9. It is evident that the introduction of Nb5+ induces a significant leap of tunability compared to the original BTW ceramics. The most pronounced improvement is in compositions x = 0.3 and x = 0.4. However, the tunability property diminishes for the x = 0.5 sample as room temperature is below its Tm. The concept of effective tunability Te has been introduced in the introduction. When the applied electric field intensity is 1 kV/mm, the calculated Te of the x = 0.3 compositions is approximately 0.634 mm/kV. That value of the x = 0.4 compositions reaches an impressive 0.805 mm/kV (although with relatively higher loss), significantly exceeding the Te reported for existing material systems. Compared to common tunable materials, the improvement in the Te of BTW-BTN is intuitively illustrated in Fig.3b. (The comparative data are all calculated also calculated under the electric field of 1 kV/mm.) Moreover, the figure of merit (FOM) is also a common parameter used to evaluate the quality of dielectric tunable materials and is defined as the ratio of tunability to dielectric loss. Figure 3c compares the FOM values of common tunable materials with those of the BTW-BTN ceramics. It can be seen that due to its extremely low loss of 10−3, BTW-BTN exhibits a much higher FOM value than common materials.
Figure 3d shows the comparison between our study with Ba0.65Sr0.35TiO3 (BST65), Ba0.6Sr0.4TiO3 (BST60), and Pb0.3Sr0.7TiO3 (PST30), which are the most representative tunable material with similar permittivity to our study37,38. Under the premise of similar dielectric constants, the dielectric loss of BTW-BTN is lower, and the bias voltage required to achieve the same tunability is lower. For example, if applied as an adjustable capacitor, to reduce the capacitance values of five materials of the same size and thickness by half, the applied bias electric fields are ~4.3 kV/cm(x = 0.4), ~7 kV/cm(x = 0.3), ~9 kV/cm(BST65), ~12 kV/cm(PST30), ~17 kV/cm(BST60), respectively. The fabrication of practical phase shifters involves various complex factors, and different devices have specific impedance-matching requirements and maximum dielectric constant requirements5,39,40. Due to the relatively high relative dielectric constant of BTW-BTN materials, further comprehensive research is needed for their practical applications in phase shifters. However, compared to the extensively researched BST60 ceramic, where the maximum dielectric constant is as high as 7200, BTW-BTN ceramics, particularly the 0.7BTW-0.3BTN composition, offer similar dielectric constants with lower dielectric loss and a relative tunability three times that of BST60. Modifications to reduce dielectric constant in BST systems, such as organic-inorganic composites and spark plasma sintering of thin films, have been well developed37,41,42,43,44,45,46,47,48,49. It can be foreseen that similar methods can be applied to 0.7BTW-0.3BTN ceramics to achieve effective tunability surpassing that of BST-based ceramics while reducing the dielectric constant.
To explore the origin of the significant tunability in BTW-BTN ceramics, neutron powder diffraction (NPD) Rietveld refinement and high-resolution transmission electron microscopy (HRTEM) observations were performed on the composition with the highest tunability, 0.6Bi6Ti5WO22−0.4Bi6Ti4Nb2O22. The results are shown in Fig. 4. Figure 4a–c displays the refined NPD patterns at three different temperatures (25 °C, 50 °C, and 100 °C) corresponding to different stages in the dielectric constant curves in Fig. 4d. Detailed crystal information and refinement results are listed in Supplementary Table 1 to 4. The refined patterns at various temperatures illustrate 0.6Bi6Ti5WO22−0.4Bi6Ti4Nb2O22 trends to normal thermal expansion above 25 °C. Unit cell parameters increase to a certain extent with temperature, maintaining an orthogonal phase structure of a ≈ c > b. The differences in the unit cell parameters between 25 °C and 200 °C are less than 0.01 Å. HRTEM images at room temperature (Fig. 4e) reveal denser and clearer nanoscale polar regions and twin boundaries than those observed in pure BTW (the comparison is shown in Supplementary Fig. 10). Enlarged images display distinctive alternating bright and dark stripes (highlighted in purple) with an average width of approximately 5.2 Å. This nanoscale domain structure may result in higher grain boundary charges and energy, thereby enhancing the dielectric constant and reducing relaxation behavior. Simultaneously, the control exerted by a direct current voltage on this reversible polarization behavior readily induces the rearrangement of these domain structures, leading to significant dielectric tunability.
DFT simulation calculations revealed the contribution of asymmetric structures and ion substitution to polarization (Fig. 5). Previous reports have shown that both TiO6 octahedron, WO6 octahedron, and BiO12 polyhedron contribute to overall polarization in the pnn2 structure32. This work quantitatively presents the polarization enhancement brought by the orthogonal phase structure. Compared with the BTW (34) model, which replaces two-thirds of Ti4+ with W6+ on the cubic phase BiTiO3 base oil in space group 34, BTW (3) model, which uses orthogonal phase Bi6Ti5WO22, the calculated total polarization increases by approximately~11.2 μC/cm2. The BTN (3) model (see Supplementary Fig. 11), based on BTW (3), replaces substitution.
Discussion
A series of solid solution ceramics (1-x)Bi6Ti5WO22−xBi6Ti4Nb2O22 (0 ≤ x ≤ 0.6), with different phase transition temperatures were successfully prepared through ion substitution design. Characterization of ferroelectric/dielectric properties reveals that through the incorporation of Nb5+ with a larger radius, the Tm of BTW ceramics increases, the dielectric constant increases, the dielectric loss is maintained at a very low level, and the dielectric tunability is greatly improved. As a dielectric tunable material, its transcendence in various parameters, including effective tunability, makes it expected to replace the BST solid solution ceramics and promote the wider application of tunable materials in microwave dielectrics and sensor devices.
Methods
Sample preparation
Dense lead-free ceramics with the composition of (1-x)Bi6Ti5WO22−xBi6Ti4Nb2O22 (0 ≤ x ≤ 0.6) were prepared using the conventional high-temperature solid-state reaction method. The raw powder materials included bismuth oxide (Bi2O3, 99%), tungsten oxide (WO3, 99%), titanium dioxide (TiO2, 99.8%), and niobium oxide (Nb2O5, 99.9%). Before weighing, all materials underwent initial sintering at 300 °C to remove moisture. Based on process experience, the Bi elements in the composition were weighed at a deficiency of 1.6%. After ball milling in ethanol solvent for 6 hours, the obtained powder was dried and preheated for 4 hours. Subsequently, secondary ball milling was performed under the same conditions. The shaping(ϕ10 mm × 1 mm) process employed a cold isostatic pressing (IP) technique at 200 MPa. The pressed particles were then sintered in the range of 920 °C to 1050 °C for 4 hours, resulting in the final desired ceramic specimens. All the tests and characterizations in our work were conducted based on samples obtained at the optimal sintering temperature (samples of the maximum density). Specifically, the sintering temperature for compositions x = 0 and x = 0.1 was 1000 °C, for x = 0.2 it was 1020 °C, for x = 0.3 and x = 0.4 it was 1030 °C, and for x = 0.5 and x = 0.6 it was 1050 °C.
Structure characterizations
The determination of the phase structure of the material was obtained through X-ray powder diffraction and in-situ neutron diffraction. X-ray diffraction was conducted using a Rigaku D/MAX-2400 with Cu Kα radiation and a PXIcel 1D detector, utilizing Cu Kα1 radiation. The data collection spanned the angular range of 10 ≤ 2θ/° ≤ 120, employing a step size Δ2θ = 0.008°. Neutron diffraction at different temperatures from 25 °C to 200 °C was performed using the high-resolution powder diffractometer ECHIDNA at ANSTO. The data collection spanned the angular range of 8 ≤ 2θ/° ≤ 160, employing a step size Δ2θ = 0.05° and a wavelength of 1.622 Å. The combination of PXRD and NPD data underwent Rietveld refinements using the GSAS program, and the peak shape function developed by van Laar and Yelon was applied50,51. Density measurements were determined by sintering large blocks of ceramic samples using the Archimedean displacement method. The relative density was obtained by comparing the measured density with the theoretical density obtained through Rietveld refinement.
Electron microscopy studies
The microstructure of the ceramics was observed by a field-emission scanning electron microscopy (FE-SEM, FEI Quanta 250 FEG, Hillsboro, Oregon, USA) operating at 30 kV. Before SEM measurements, the sample underwent flat polishing with diamond suspension and was re-calcined at 950 °C for 30 minutes as a hot etching step. The images from the HRTEM (high-resolution transmission electron microscopy) and the HAADF-STEM (high-angle annular dark-field scanning transmission electron microscopy) were obtained using a JEOL F200 and an FEI Cubed Themis G2, respectively. The accelerating voltages used for imaging were 200 kV and 300 kV, respectively.
Ferroelectric and dielectric measurements
The ferroelectric properties, particularly the polarization-electric field (P-E) loops at different temperatures, were investigated using a probe station equipped with a Precision Premier II Ferroelectric Tester from Radiant Technologies. Before testing, the ceramic samples were meticulously polished to produce thin ceramic layers with a thickness of approximately 0.1 mm. Electrodes were fabricated on the ceramic surface using gold sputtering, with a sputtering time of 2 minutes and an electrode thickness of less than 100 nm. The dielectric spectra over a wide frequency range (from 102 Hz to 107 Hz) and temperature range (−200 °C to +100 °C) were systematically recorded using an LCR spectrometer (HP4980, Agilent) coupled with a temperature control system (CRYO 610 L). Before testing, low-temperature silver paste was applied to the two polished and smooth surfaces of the sintered sample. The sample was then fired at 55 °C for 30 minutes to create the electrodes. Reversible nonlinear dielectric measurements at a frequency of 10 kHz were conducted using a self-assembled test circuit system. This system comprised a DC voltage stabilizer(SRS350), impedance analyzer(TH2828S), and protective circuit.
PFM Measurements
The atomic force microscopy tests were conducted using the instrument MFP-3D with a bias voltage module, manufactured by Asylum Research, USA. The samples used in the experiments were sheet samples, and the surfaces were thoroughly polished and polished before testing.
DFT calculations
The first-principles calculations are carried out using GPAW52 with the Perdew-Burke-Ernzerhof (PBE) exchange-correlation functional53. To ensure convergence, when performing Brillouin-zone integration on a 4 × 4 × 4 mesh, we set the energy cutoff of 750 eV. Structural relaxations are performed until forces on all atoms are less than 0.05 eV/Å, with an energy convergence criteria set to 5 × 10−4 eV. Subsequently, the polarization of each relaxed configuration was calculated using the Berry phase approach54. We also calculated the Born effective charge using GPAW, and used it to calculate the polarization as P = Σdi·Zi*/V, where di is the cation polar displacement, Zi* is the Born effective charge of the ions, and V is the volume of the unit cell55. These calculations were conducted on Pnn2 of Bi6Ti5WO22 and Bi6Ti4Nb2O22, with a pseudo-cubic constraint indicated by Pn−3.
Data availability
All data supporting the findings are provided as figures and accompanying tables in the article and Supplementary Information. The data that support the findings of this study are available from the corresponding authors.
References
Gao, F., Zhang, K., Guo, Y., Xu, J. & Szafran, M. (Ba, Sr) TiO3/polymer dielectric composites–progress and perspective. Prog. Mater. Sci. 121, 100813 (2021).
Huang, W. et al. Ultrahigh recoverable energy storage density and efficiency in barium strontium titanate-based lead-free relaxor ferroelectric ceramics. Appl. Phys. Lett. 113, 203902 (2018).
Selmi, A., Mascot, M., Jomni, F. & Carru, J. Investigation of interfacial dead layers parameters in Au/Ba0.85Sr0.15TiO3/Pt capacitor devices. J. Alloy. Compd. 826, 154048 (2020).
Solodukha, A. & Grigoryan, G. Negative capacitance effect in the low-frequency impedance of barium strontium titanate semiconductor ceramics. Inorg. Mater. 55, 401–404 (2019).
Yu, S., Li, L., Zheng, H., Sun, Z. & Zhang, W. Ba0.6Sr0.4TiO3−Bi1.5Mg1.0Nb1.5O7 composite thin film capacitors with enhanced tunable performance for tunable device applications. Mater. Lett. 161, 517–519 (2015).
Zhang, Q., Zhai, J. & Yao, X. Low loss, high tunability of Ba0.4Sr0.6TiO3−Mg3B2O6 microwave composite ceramics. J. Am. Ceram. Soc. 93, 2560–2562 (2010).
Hu, G., Gao, F., Liu, L., Xu, B. & Liu, Z. Microstructure and dielectric properties of highly tunable Ba0.6Sr0.4TiO3/MgO/Al2O3/ZnO composite. J. Alloy. Compd. 518, 44–50 (2012).
Gim, Y. et al. Microstructure and dielectric properties of Ba1-xSrxTiO3 films grown on LaAlO3 substrates. Appl. Phys. Lett. 77, 1200–1202 (2000).
Jiao, T. et al. High tunability and low loss via establishing an internal electric field in LiFe5O8/Ba0.6Sr0.4TiO3 composite films using chemical solution deposition method. Appl. Surf. Sci. 590, 153112 (2022).
Yu, S., Zhang, C., Wu, M., Dong, H. & Li, L. Ultra-high energy density thin-film capacitors with high power density using BaSn0. 15Ti0.85O3/Ba0.6Sr0.4TiO3 heterostructure thin films. J. Power Sources 412, 648–654 (2019).
Chung, U. et al. Low-losses, highly tunable Ba0.6Sr0.4TiO3/MgO composite. Appl. Phys. Lett. 92, 042902 (2008).
Cui, J., Dong, G., Yang, Z. & Du, J. Low dielectric loss and enhanced tunable properties of Mn-doped BST/MgO composites. J. Alloy. Compd. 490, 353–357 (2010).
He, Y., Xu, Y., Liu, T., Zeng, C. & Chen, W. Microstructure and dielectric tunable properties of Ba0.6Sr0.4TiO3−Mg2SiO4-MgO composite. IEEE Trans. Ultrason., Ferroelectr., Freq. Control 57, 1505–1512 (2010).
Lee, O. et al. Extremely high tunability and low loss in nanoscaffold ferroelectric films. Nano Lett. 12, 4311–4317 (2012).
Liu, P. et al. Preparation and dielectric properties of BST−Mg2TiO4 composite ceramics. Mater. Chem. Phys. 114, 624–628 (2009).
Zhang, J., Zhai, J., Chou, X. & Yao, X. Relaxor behavior and dielectric properties of (1-x)Ba0.6Sr0.4TiO3−xMg0.7Zn0.3TiO3 composite ceramics for tunable microwave applications. Solid State Commun. 147, 392–396 (2008).
Wu, J., Wang, X., Fan, Y., Shi, X. & Lu, W. Microstructures and dielectric properties of Ba0.6Sr0.4TiO3−MgO ceramics prepared by non-aqueous gelcasting and dry pressing. Mater. Res. Bull. 46, 2217–2221 (2011).
Wang, T., Gao, F., Hu, G. & Tian, C. Synthesis Ba0.6Sr0.4TiO3−ZnNb2O6 composite ceramics using chemical coating method. J. Alloy. Compd. 504, 362–366 (2010).
Wang, H., Dong, Y. & Wang, Z. High tunable dielectric properties of Zn and Mg alternately doped Ba0.6Sr0.4TiO3 film varactors. J. Alloy. Compd. 745, 651–658 (2018).
Vilarinho, P., Fu, Z., Kingon, A. & Tkach, A. Low loss tunable dielectric BaNd2Ti5O14−(Ba0.5Sr0.5)TiO3 composite thick films. Scr. Mater. 155, 160–163 (2018).
Lu, X., Tong, Y., Zhang, L., Ma, B. & Cheng, Z. High dielectric tunability in composites prepared using SiO2 coated Ba0.5Sr0.5TiO3 nanoparticles. Ceram. Int. 44, 9875–9879 (2018).
Hughes, H., Iddles, D. & Reaney, I. Niobate-based microwave dielectrics suitable for third generation mobile phone base stations. Appl. Phys. Lett. 79, 2952–2954 (2001).
Jang, H. W. et al. Domain engineering for enhanced ferroelectric properties of epitaxial (001) BiFeO thin films. Adv. Mater. 21, 817–823 (2009).
Kang, B., Park, B., Bu, S., Kang, S. & Noh, T. Different fatigue behaviors of SrBi2Ta2O9 and Bi3TiTaO9 films: Role of perovskite layers. Appl. Phys. Lett. 75, 2644–2646 (1999).
Kong, L. et al. Electrically tunable dielectric materials and strategies to improve their performances. Prog. Mater. Sci. 55, 840–893 (2010).
Lu, J. & Stemmer, S. Low-loss, tunable bismuth zinc niobate films deposited by rf magnetron sputtering. Appl. Phys. Lett. 83, 2411–2413 (2003).
Panda, P. Environmental friendly lead-free piezoelectric materials. J. Mater. Sci. 44, 5049–5062 (2009).
Puli, V., Pradhan, D., Pérez, W. & Katiyar, R. Structure, dielectric tunability, thermal stability and diffuse phase transition behavior of lead free BZT–BCT ceramic capacitors. J. Phys. Chem. Solids 74, 466–475 (2013).
Yun, K., Noda, M. & Okuyama, M. Prominent ferroelectricity of BiFeO3 thin films prepared by pulsed-laser deposition. Appl. Phys. Lett. 83, 3981–3983 (2003).
Zhang, X., Song, Q., Xu, F. & Ong, C. Dielectric dispersion of BiFeO3 thin film over a broad frequency range (100 Hz − 10 GHz). Appl. Phys. Lett. 94, 022907 (2009).
Jardiel, T., Caballero, A., Fuentes, L. & Villegas, M. Preparation and properties of Bi6Ti5WO22: a new phase in the Bi2O3−TiO2−WO3 system. J. Mater. Sci. 44, 5824–5828 (2009).
Li, R. et al. Ultralow loss and high tunability in a non‐perovskite relaxor ferroelectric. Adv. Funct. Mater. 33, 2210709 (2023).
Liu, X., Yin, J. & Wu, J. A new class of ion substitution to achieve high electrostrain under low electric field in BNT‐based ceramics. J. Am. Ceram. Soc. 104, 6277–6289 (2021).
Shannon, R. Dielectric polarizabilities of ions in oxides and fluorides. J. Appl. Phys. 73, 348–366 (1993).
Kikuchi, T. Synthesis of new, layered bismuth titanates, Bi7Ti4NbO21 and Bi6Ti3WO18. J. Less Common Met. 48, 319–323 (1976).
Wu, T., Pu, Y., Gao, P. & Liu, D. Influence of Sr/Ba ratio on the energy storage properties and dielectric relaxation behaviors of strontium barium titanate ceramics. J. Mater. Sci.: Mater. Electron. 24, 4105–4112 (2013).
Somiya, Y., Bhalla, A. & Cross, L. Study of (Sr, Pb)TiO3 ceramics on dielectric and physical properties. Int. J. Inorg. Mater. 3, 709–714 (2001).
Liu, W. et al. Enhanced dielectric tunability and reduced dielectric loss in the La/Fe co-doped Ba0.65Sr0.35TiO3 ceramics. J. Alloy. Compd. 901, 163642 (2022).
Altynnikov, A., Gagarin, A., Tumarkin, A. & Kotel’nikov, I. Characterization of the properties of barium–strontium titanate films and controlled elements based on them in the frequency range of 1 − 60 GHz. Tech. Phys. Lett. 45, 540–543 (2019).
Kim, D., Choi, Y., Allen, M., Kenney, J. & Kiesling, D. A wide-band reflection-type phase shifter at S-band using BST coated substrate. IEEE Trans. Microw. Theory Tech. 50, 2903–2909 (2002).
Liu, S. et al. (Ba0.6Sr0.4) TiO3/PEEK composites modified by polyethersulfone with low dielectric constant and high dielectric tunability under DC bias. Compos. Sci. Technol. 233, 109929 (2023).
Li, K., Wang, H., Xiang, F., Liu, W. & Yang, H. Surface functionalized Ba0.6Sr0.4TiO3/poly (vinylidene fluoride) nanocomposites with significantly enhanced dielectric properties. Appl. Phys. Lett. 95, 202904 (2009).
Tang, H. & Sodano, H. Ultra high energy density nanocomposite capacitors with fast discharge using Ba0.2Sr0.8TiO3 nanowires. Nano Lett. 13, 1373–1379 (2013).
Wang, H., Xiang, F. & Li, K. Ceramic-polymer Ba0.6Sr0.4TiO3/poly (methyl methacrylate) composites with different type composite structures for electronic technology. Int. J. Appl. Ceram. Technol. 7, 435–443 (2010).
Zhang, L., Qiao, Q., Yue, Z., Yang, F. & Li, L. A new HDPE/BST polymer-ceramic composite for wireless temperature sensing. Ceram. Int. 41, S471–S475 (2015).
Zhang, Q. et al. Enhanced dielectric tunability of Ba0.6Sr0.4TiO3/Poly (vinylidene fluoride) composites via interface modification by silane coupling agent. Compos. Sci. Technol. 129, 93–100 (2016).
Gu, Z. et al. Resonant domain-wall-enhanced tunable microwave ferroelectrics. Nature 560, 622–627 (2018).
Lee, C. et al. Exploiting dimensionality and defect mitigation to create tunable microwave dielectrics. Nature 502, 532–536 (2013).
Guo, Y. et al. Characterization and performance of plate-like Ba0.6Sr0.4TiO3/Poly (vinylidene fluoride–trifluoroethylene-chlorotrifluoroethylene) composites with high permittivity and low loss. Polymer 203, 122777 (2020).
Arlt, G. Twinning in ferroelectric and ferroelastic ceramics: stress relief. J. Mater. Sci. 25, 2655–2666 (1990).
Parsons, S. Introduction to twinning. Acta Crystallogr. Sect. D: Biol. Crystallogr. 59, 1995–2003 (2003).
Enkovaara, J. et al. Electronic structure calculations with GPAW: a real-space implementation of the projector augmented-wave method. J. Phys.: Condens. Matter 22, 253202 (2010).
Perdew, J., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865 (1996).
King-Smith, R. & Vanderbilt, D. Theory of polarization of crystalline solids. Phys. Rev. B 47, 1651 (1993).
Resta, R., Posternak, M. & Baldereschi, A. Towards a quantum theory of polarization in ferroelectrics: The case of KNbO3. Phys. Rev. Lett. 70, 1010 (1993).
Acknowledgements
We thank the National Key R&D Program of China (2021YFB3800602) (D. Z.), the National Natural Science Foundation of China (51972260, 52072295, 62175056) (D. Z.), and (52202146) (D. X.), the International Cooperation Project of Shaanxi Province (2021KWZ-10) (D. Z.), the Fundamental Research Funds for the Central University, the 111 Project of China (B14040) (D. Z.). The SEM work was done at the International Center for Dielectric Research (ICDR), Xi’an Jiaotong University, Xi’an, China. The authors thank Dr. Yan-Zhu Dai for her help with SEM.
Author information
Authors and Affiliations
Contributions
R.L. proposed the idea, developed the concept, synthesized all materials, and conducted characterizations. D.X. performed TEM imaging and related analyses. Q.M. and X.L. assisted in AFM testing. F.Z., D.W. and Z.S. conducted simulation and computational modeling work. W.L. assisted in dielectric performance testing. R.L., C.D. and D.Z. were the primary writers of the paper and the principal investigators. All authors discussed the results and provided feedback on the paper.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks Fu-Hsing Lu, Brajendra Singh and the other anonymous reviewer(s) for their contribution to the peer review of this work. A peer review file is available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Li, R., Xu, D., Du, C. et al. Giant dielectric tunability in ferroelectric ceramics with ultralow loss by ion substitution design. Nat Commun 15, 3754 (2024). https://doi.org/10.1038/s41467-024-48264-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-024-48264-7
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.