Abstract
The oxidative dehydrogenation of propane, primarily sourced from shale gas, holds promise in meeting the surging global demand for propylene. However, this process necessitates high operating temperatures, which amplifies safety concerns in its application due to the use of mixed propane and oxygen. Moreover, these elevated temperatures may heighten the risk of overoxidation, leading to carbon dioxide formation. Here we introduce a microchannel reaction system designed for the oxidative dehydrogenation of propane within an aqueous environment, enabling highly selective and active propylene production at room temperature and ambient pressure with mitigated safety risks. A propylene selectivity of over 92% and production rate of 19.57 mmol mCu−2 h−1 are simultaneously achieved. This exceptional performance stems from the in situ creation of a highly active, oxygen-containing Cu catalytic surface for propane activation, and the enhanced propane transfer via an enlarged gas-liquid interfacial area and a reduced diffusion path by establishing a gas-liquid Taylor flow using a custom-made T-junction microdevice. This microchannel reaction system offers an appealing approach to accelerate gas-liquid-solid reactions limited by the solubility of gaseous reactant.
Similar content being viewed by others
Introduction
Propylene (C3H6) serves as a crucial feedstock within the petrochemical industry, with its primary production methods being steam cracking and fluid catalytic cracking (FCC)1,2,3. However, these conventional methods are being stretched by the escalating global demand for propylene4,5. The propane (C3H8) dehydrogenation (PDH) process, capitalizing on the abundant propane in shale gas, has been developed to bridge this supply-demand gap6,7. Nevertheless, the PDH process suffers from drawbacks including its endothermic nature requiring substantial energy input, and rapid catalyst deactivation due to coke formation5,8. Oxidative dehydrogenation of propane (ODHP) presents an appealing alternative. This process is exothermic, allowing it to operate at lower temperatures and reducing energy requirements9,10,11. Additionally, the presence of oxygen (O2) in ODHP suppresses the coke formation on the catalysts, and thus extending their lifetime12,13. A central research theme of ODHP is the development of highly selective catalytic system for propylene formation while concurrently inhibiting its consecutive overoxidation to form carbon dioxide (CO2). The typical selectivity of propylene in ODHP process using conventional metal oxide catalysts, such as vanadium- and chromium-based materials, is less than 70% at typical experimental conditions (400-500 °C and 1 atm)14. Recently, boron-containing materials, including supported boron oxide, hexagonal boron nitride, and boron-doped zeolites, have been reported to selectively produce propylene with suppressed CO2 formation in ODHP process15,16,17,18,19,20,21. Alkanes are proposed to be activated on boron-based reaction sites via a radical mechanism, which typically requires temperatures exceeding 500 °C to achieve substantial rates22,23. The high operating temperature fails to take adavange of the strong thermodynamic driving force in ODHP, and enhances the mobility of hydroxylated boron centers, causing catalyst deactivation24,25. Moreover, high temperature reactions employing a mixture of alkane and oxygen carry safety risks, especially at large scale.
The key to addressing the challenges in ODHP lies in the development of efficient reaction system that can achieve high selectivity and activity in propylene production at low temperatures (e.g., <200 °C). We recently identified an aqueous reaction system that uses copper (Cu) powder as the catalyst and O2 as the oxidant, demonstrating the capability to activate light alkanes at room temperature and ambient pressure with appreciable rates26. Notably, with a batch reactor, propane can be transformed into propylene with up to 94% selectivity and a production rate of 0.71 mmol mCu−2 h−1. However, the inefficient mass transfer of propane due to its low solubility in the aqueous solution (~1.1 mmol L−1) hinders the further enhancement of reaction efficiency for practical implementation and complicates kinetic analysis for mechanistic understanding. In addition, the use of C3H8 and O2 mixture still presents a safety risk in operation.
Herein, we report a microfluidic reaction system with a Cu microtube serving as both the catalyst and the microchannel reactor to simultaneously address the issues of inefficient mass transport and safety risk, achieving a 27-fold increase in reactivity compared to a batch reactor while maintaining the propylene selectivity over 92%. We used a custom-made T-junction microdevice to disperse gaseous reactants (C3H8 + O2) into a sulfuric acid (H2SO4) solution, which formed a gas-liquid Taylor flow prior to entering the Cu microtube. Flow pattern analysis assisted by high-speed camera imaging reveals a substantial enhancement in mass transfer, which can be attributed to the increased gas-liquid interfacial area and a shortened diffusion path for the reactant gas to reach the Cu surface. Importantly, our system also mitigates the potential explosion risk associated with the C3H8 + O2 mixture, as the gaseous mixture is segmented into small millimeter-scale portions by plugs of aqueous solution. We conducted kinetic investigations to determine the reaction orders and apparent activation energy. Density functional theory (DFT) calculations were also carried out to explore the reaction pathways leading to the formation of propylene and other minor products (i.e., n/i-propanol). Our microfluidic system demonstrates high selectivity and activity in producing propylene from propane at room temperature and ambient pressure. This approach presents a promissing pathway for enhancing reactivity of other gas-liquid-solid multiphase reactions, particularly those hindered by the low solubility of gaseous reactants in a liquid medium, such as H2O2 synthesis using H2 and O227,28, aerobic alcohol oxidation using O229,30,31, and electrochemical conversion of CO232,33,34, O235,36,37, and N238,39 on metallic catalyst surfaces.
Results
Gas-liquid Taylor flow in a Cu microtube reactor
A commercial Cu microtube with an inner diameter of 550 μm and length of 3 m was used as the tubular microchannel reactor, with its inner surface as catalyst. The morphology and chemical composition of Cu microtube were characterized using scan electron microscopy (SEM) equipped with energy dispersive spectroscopy (EDS) (Supplementary Fig. 1). Prior to entering the Cu microtube reactor, the reactant gases, composed of C3H8 and O2 with a predetermined ratio, were dispersed into the aqueous H2SO4 solution using a custom-made capillary embedded step T-junction microdevice40 (see Supplementary Fig. 2 for the scheme of the experimental setup). This results in the formation of a stable gas-liquid Taylor flow (Fig. 1a), as recorded by a high-speed camera in transparent polypropylene tubes connected to both ends of the Cu microtube with the identical diameter. This Taylor flow pattern in microchannel, containing Taylor bubbles, liquid plugs, and thin liquid film between every Taylor bubbles and inner surface, has been demonstrated to significantly enhance mass transfer characteristic of gas molecules due to the large interfacial area, special circulation flow field and the short path required for molecular diffusion across the liquid film40,41,42,43. In addition, Taylor flow is characterized for its uniformity, making it suitable for conducting mass transport characteristic analyses. Other flow patterns such as bubbly flow and annular flow (Supplementary Fig. 3), have limitations in propane activation: the bubbly flow, while increasing the interfacial area, does not reduce the diffusion path, and the annular flow, with an extremely low liquid to gas ratio, does not provide a sufficient liquid supply necessary for propane activation.
The flow patterns as well as the mass transfer characteristics, i.e., thickness of liquid film and gas-liquid interfacial area, were investigated at various liquid flow rates and gas flow rates. Decreasing the liquid flow rates at a fixed total flow rate of C3H8 + O2 of 2 mL min−1 maintains the pattern of Taylor flow unchanged but elongates the gas bubbles (Fig. 1b), which essentially increases the gas-liquid interfacial area per unit of volume (Fig. 1c) calculated based on the dimensions of the gas and liquid components in Taylor flow (see Supplementary Note 1 for details) and promotes the dissolution of gas molecules to the liquid phase44,45. This gas-liquid interfacial area can reach a value of ~8000 m2/m3, as opposed to only ~100 m2/m3 for conventional batch reactors used in chemical processes46, highlighting the enhanced mass transfer in the Cu microtube reactor. The liquid film thickness decreases as the liquid flow rate decreases (Fig. 1d), facilitating the diffusion of dissolved gas molecules to the Cu catalyst surface. The increase of gas-interfacial area and decrease of thickness of liquid film both improve the mass transfer of the gaseous reactants to the Cu surface. We also investigated the mass transfer characteristics at different gas flow rates with a fixed liquid flow rate of 0.2 mL min−1. Increasing the gas flow rates enlarges the gas-interfacial area and reduces the thickness of liquid film (Supplementary Fig. 4), thus improving the mass transfer, which is in good agreement with previous studies44,45,47.
Propane activation in Cu microtube reactor
The activation of propane was then carried out in this Cu microtube reactor, which also serves as the catalyst, at ambient pressure and room temperature. The mixture of C3H8 and O2 with a molar ratio of 3:1 was used as the gas feed, and 0.5 M H2SO4 was chosen as the reaction medium. The Taylor flow was generated as described above. After passing through the Cu microtube, the gas bubbles were collected using downward displacement of water, and then analyzed using a gas chromatograph (GC), while the liquid was collected separately and analyzed using a nuclear magnetic resonance (NMR) spectrometer. Propylene was the main product of propane activation, with a selectivity up to 93% under all conditions. A small amount of methane and ethylene were also detected, which are the common side products in the oxidative dehydrogenation of propane48,49,50. Other minor liquid products, including propionic acid, acetone, i-propanol, acetic acid and formic acid were also detected. No appreciable overoxidation was observed as the combined selectivity of CO and CO2 is less than 1%.
The activation of propane in the Cu microtube was first evaluated at various liquid flow rates with a fixed gas flow rate (Fig. 2a). At a fixed gas flow rate of 2.00 mL min−1, we observed a significant increase in propane oxidation rate from 4.55 to 15.97 mmol mCu−2 h−1 as the liquid flow rate decreased from 1 to 0.25 mL min−1. The increase in propane oxidation rate at this liquid flow rate range can be attributed to the improved mass transfer as revealed by the increased gas-liquid interfacial area and decreased liquid film thickness (Figs. 1c and 1d). However, at the liquid flow rate ranging from 0.25 to 0.1 mL min−1, the propane oxidation rate plateaus, suggesting that the reaction was under kinetic control at these conditions and that any further improvement in mass transfer resulting from reducing the liquid flow rate would no longer be advantageous. The surprising decrease of reaction rate at further improved mass transfer is likely due to the decreasing concentration of H2SO4 and O2 as the Taylor flow passes through the Cu microtube, primarily due to the consumption during Cu dissolution. The reduction in the H2SO4 concentration does not affect propane oxidation rate until the supplied H2SO4 is nearly depleted (i.e., the remaining H2SO4 concentration at outlet lower than 0.1 M) as suggested by our control experiment (Supplementary Fig. 5). The decrease in liquid flow rate reduces the H2SO4 feed rate, and thus leading to a lower H2SO4 concentration at any given point in the reactor barring the inlet. At the lowest liquid flow rate of 0.05 mL min−1, the supplied H2SO4 was approaching depletion at the outlet of the reactor (Supplementary Fig. 6a), leading to a decrease in the propane oxidation rate (Fig. 2a). The O2 consumption is also increased at low liquid flow rate primarily due to the enhanced Cu dissolution resulting from improved mass transfer and extended residence time of O2 (Supplementary Fig. 6a). This is expected to reduce the propane oxidation rate as O2 is the oxidant for activating C3H8. However, this contradicts to the improved propane reaction rate at lower liquid flow rate, which is attributable to the positive influence of improved mass transfer on propane activation overweighing the negative effect of the reduced O2 concentration. We note that the flow patterns at the reactor’s outlet maintained the characteristics of Taylor flow, with slightly reduced length of the gas bubbles due to the consumption of O2 during the reaction (Supplementary Fig. 7).
Increasing the gas feed at higher flow rates can alleviate the reduction in O2 concentration along the Cu microtube and improve the oxidation of propane. At a fixed liquid flow rate of 0.2 mL min−1, the propane oxidation rate increases with the increase of gas flow rate from 2 to 10 mL min−1 (Fig. 2b), whereas the corresponding O2 conversion rate decreases from near 80% to 18% (Supplementary Fig. 6b). Notably, the highest production rate of propylene at room temperature was achieved at a liquid flow rate of 0.2 mL min−1 and gas flow rate of 10 mL min−1, reaching a value of 19.57 mmol mCu−2 h−1, this value can be further increased to 87.20 mmol mCu−2 h−1 when increasing the temperature to 40 °C. The production rates of propylene from propane achieved in our Cu microtube reactor are at least one order of magnitude higher than that of many previously reported catalysts which operates at high temperatures12,13,15,17,20,49,51,52,53,54,55,56,57 (Fig. 2c), and significantly higher than that achieved in our previous batch-type reactor26 (Supplementary Fig. 8). At this reaction condition, the Cu microtube microchannel reactor exhibits stable propylene production with over 92% selectivity in a 12-h experiment (Fig. 2d), demonstrating the stability of this reaction system, which includes both the Taylor flow and the catalyst surface for propane activation. The loss of Cu in a 12-h experiment is unlikely to significantly influence the stability of propane activation as the time for dissolving all the Cu in our Cu microreactor can be estimated to be around 346 h calculated from the Cu dissolution rate (~ 0.133 g h−1) and the mass of Cu microtube (~ 46 g). However, for practical application, the stability of the reactor itself should be taken into account. Designing stable catalysts, in which the specific active sites are immobilized on the wall of the microtube that do not rely on Cu dissolution, represents a promising strategy for improving the stability of the reactor. Increasing the gas flow rate at a fixed liquid flow rare is expected to improve the mass transport (Supplementary Fig. 4)44,45, however, this is not likely responsible for the enhanced activities as the reaction rate at the liquid flow rate of 0.2 mL min−1 is not limited by the mass transport even when the gas flow is at the lowest rate of 2 mL min−1 (Fig. 2a). The conversion of propane remains low within the gas flow rate between 2 to 10 mL min−1 (Supplementary Fig. 9). Thus, the enhanced reaction rate can be solely ascribed to the increase of O2 concentration along the Cu microtube.
Kinetic analysis of propane activation in Cu microtube reactor
The impact of reactant concentrations, i.e., partial pressure of O2 and C3H8, on the reaction rate were then investigated at a gas flow rate of 10 mL min−1 and a liquid flow rate of 0.2 ml min−1, owing to the enhanced mass transport and relatively low O2 consumption (Supplementary Fig. 10). The inert Ar gas was introduced to maintain a constant total gas flow rate when the partial pressure of propane or oxygen was adjusted separately. The propane oxidation rate exhibits first-order dependence on the partial pressure of propane when fixing the O2 partial pressure at 0.25 atm (Fig. 3a). Noting that the O2 conversion rates remained remarkably consistent across various propane partial pressures in the study of propane’s reaction order (approximately 18%). Consequently, despite its consumption, the impact of O2 on the reactions should be comparably uniform in the analysis of propane’s reaction order. The dependence of reaction rate on O2 partial pressure at the fixed propane partial pressure of 0.25 atm resembles a Langmuir chemisorption model (Fig. 3b). The Langmuir chemisorption behavior of O2 partial pressure is commonly observed in ODHP on boron-based catalysts, in which the O2 is first adsorbed onto boron sites to activate the catalysts15,17. In our system, the impact of O2 concentrations on propane activation rate is likely linked to the dissolution of Cu as its rate exhibits a similar trend as that of propane oxidation with respect to varying O2 concentrations (Supplementary Fig. 11a). An almost linear correlation between the propane activation rate and the Cu dissolution rate is revealed in Supplementary Fig. 11b, further implying that the dissolution of Cu may play a significant role in facilitating C-H activation. These mechanistic aspects will be discussed in the following sections. A higher O2 to propane ratio is beneficial for the deeper oxidation of propane, as both increasing the O2 partial pressure or decreasing the propane partial pressure lead to higher selectivities toward oxygenates, such as acetone and propionic acid (Supplementary Fig. 12). The apparent activation energy with a value of 76.21 kJ mol−1 was determined in the temperature range of 298 to 313 K, which is close to the typical values obtained in oxidative dehydrogenation of propane13,15,50. A slight increase in the selectivity of propylene was observed at elevated temperature (Supplementary Fig. 13), likely due to the facilitated desorption of propylene from Cu surface5,58. High performance combining a selectivity of 94% and a production rate of 87.20 mmol mCu−2 h−1 of propylene was achieved at 313 K. Control experiment using propylene as substrate only produces a small amount of allyl alcohol (Supplementary Fig. 14), suggesting that propylene was not an intermediate in route to oxygenates (except for allyl alcohol) or CO2 in propane activation.
Computational investigations for mechanistic understanding
To explore the origin of high selectivity of propylene in propane activation, DFT calculations were carried out to explore reaction pathways toward propylene and other minor product formations on Cu surface in acidic environment. Both kinetics and thermodynamics were considered. Cu2O was selected as the model surface for DFT calculation in this reaction framework, which was justified by the fact that a thin Cu2O layer readily forms on Cu surfaces upon contact with O2 molecules as evidenced by both experimental and theoretical investigations reported in literature26,59,60. The possible role of Cu2+ on propane activation can be ruled out by the fact that no products produced when conducting the control experiment that containing 0.2 M CuSO4 and 0.5 M H2SO4 in the liquid flow using a polypropylene tube rather than Cu microtube as the reactor (Supplementary Fig. 15). As shown in Fig. 4, the initial propane activation can proceed through the cleavage of either primary or secondary C-H bond, leading to the formation of a Cu bound n-propyl or i-propyl and an adjacent surface hydroxyl group (Fig. 4, Supplementary Fig. 16 and 17). This finding is in line with previous studies on ODHP, underscoring the cleavage of both primary and secondary C-H bond to be the key step in activating propane15,23,24,50. The initial cleavage of both primary and secondary C-H bonds is exothermic and kinetically facile, with energy barriers of only 0.23 and 0.26 eV, respectively, which can be easily surmounted at ambient conditions. Following this, protons in acidic solutions react with the surface hydroxyl group to form water which desorbs from the surface, leaving behind a positively charged surface with an oxygen vacancy. This vacancy can be readily filled by O2 molecules with ΔG = -1.77 eV. The resulting positively charged surface exhibits the capability for further C-H cleavage of the adsorbed propyl to form propylene, or C-O bond formation to form propanol. The energy barriers of the further C-H bond cleavage or C-O bond formation along the n-propyl pathway are 0.36 and 1.20 eV, whereas those along the i-propyl pathway are 0.33 and 0.92 eV, respectively. The energy barriers for further C-H bond cleavage on both two pathways are considerably lower than those for C-O bond formation, aligning with the experimental results that the selectivity of propylene is significantly higher than that of oxygenates during propane activation. Upon the formation of propylene and propanol, the resulting protonated surface reacts with the protons and dissolves the Cu2+ ions, exposing fresh Cu surface to react with O2 to form Cu oxide layer for subsequent propane activation. These results suggest a coupling between propane activation and Cu dissolution, explaining the observed consistency between propane activation and Cu dissolution rates across various O2 partial pressures (Fig. 3b and Fig. S7).
Discussion
In this study, we developed a Cu microtube reactor in conjunction with gas-liquid Taylor flow enabling efficient propylene production via propane activation at room temperature and ambient pressure. The exceptional performance observed can be attributed to significantly improved mass transport, facilitated by a substantial gas-interfacial area and a minimized path for reactant diffusion to the catalyst surface within the gas-liquid Taylor flow. The Taylor flow, obtained by the T-junction microdevice, demonstrated noteworthy stability, promoting the continuous production of propylene with an impressive selectivity exceeding 92% over a duration of at least 12 hours. We further demined key kinetic variables, such as reaction orders and apparent activation energy, enabled by the enhanced mass transfer. DFT calculations reveal that the propane activation process is coupled with a facile Cu dissolution reaction, aligning with observed trends where the dependence of propane activation rate and Cu dissolution rate on O2 concentration marked similarly. Both computational and experimental analyses show a proclivity of this reaction system toward the production of olefins over oxygenates, suggesting the potential for the production of long-chain alkenes, which are important platform chemicals predominantly derived from petroleum. This strategy can be extended to facilitate other multiphase reactions involving reactants with low solubility in a liquid medium. The microfluidic reaction system presents scalability advantages, as it can be easily upscaled using multiple microchannels in parallel with a shared flow. Importantly, our system also mitigates the potential explosion risk associated with flammable gas and oxygen mixture, as the gaseous mixture is segmented into small millimeter-scale portions by plugs of aqueous solution. While recognizing that propane conversion in this system remains modest, effective strategies to overcome this limitation include the development of a packed bed reactor that integrates larger Cu catalyst surfaces, in conjunction with microfluidic flow, and operates at higher temperatures. Importantly, future efforts should also focus on the design of stable catalysts featuring specific active sites that do not rely on Cu dissolution. This approach not only aims to reduce Cu consumption during propane activation but also represents a promising avenue for advancing research in this field.
Methods
Materials
Cu tube (Zhongxin Metal Materials, 550 μm inner diameter, 99.9%), sulfuric acid (Sigma, ACS reagent, 95.0-98.0%), Cu powder (Sigma-Aldrich, dendritic, <45 μm, 99.7% trace metals basis), propane (Air Liquide, 99.9%), O2 (Air Liquide, 99.999%), Ar (Air Liquide, 99.999%), propylene (Air Liquide, 99.99%). Deionized water in all experiments was prepared from a Millipore system (18.2 MΩ·cm)
Gas-liquid Taylor flow formation
Commercial Cu microtubes with inner diameter of 550 μm and length of 3 m were used as microchannel reactors for all experiments unless noted otherwise. Two transparent polypropylene tubes with identical diameter were connected to both ends of the Cu microtube for capturing the flow pattern. Prior to entering the Cu microtube, the reactant gases, composed of C3H8 and O2 with a predetermined ratio, were dispersed with aqueous H2SO4 solution using a custom-made capillary embedded step T-junction microdevice40. The flow rates of C3H8 and O2 were controlled by mass flow controllers (MKS Instruments Inc.) and calibrated by an ADM flow meter (Agilent Technologies). The flow rate of aqueous H2SO4 solution was controlled by a syringe pump (Chemyx Inc.) and calibrated by a graduated cylinder. After passing through the Cu microtube, the gas components in the flow were collected using downward displacement of water, while the liquid was collected separately using a vial. The flow pattern was captured using a high speed camera (i-SPEED TR, Olympus) with a fixed frame rate of 2000 fps after the flow system was allow to stabilize for at least 5 minutes. The flow patterns as well as the mass transfer characteristics, i.e., thickness of liquid film and gas-liquid interfacial area, were then determined upon the recorded photos (Supplenmantary Note 1).
Propane activation in a microchannel reactor
The activation of propane was carried out in the above-mentioned Cu microtube reactor which also served as the catalyst. The Cu microtube was firstly washed by delivering 0.5 M H2SO4 solutions with a flow rate of 0.5 mL min−1 for 10 minutes to remove the native oxides. Before reaction, five minutes was arranged for the gas-liquid system to stabilize. The mixture of C3H8 and O2 with a molar ratio of 3:1 was used as the gas feed, and 0.5 M H2SO4 was chosen as the reaction medium. For experiments at various liquid flow rates from 0.05 mL min−1 to 1 mL min−1, the C3H8 + O2 gas flow rate was fixed at 2 mL min−1. For experiments at various gas flow rates from 2 mL min−1 to 10 mL min−1, the liquid flow rate was fixed at 0.2 mL min−1. For experiments at various C3H8 and O2 partial pressures, the total gas flow rate and liquid flow rate were fixed at 10 mL min−1 and 0.2 mL min−1, respectively. The inert Ar gas was introduced to maintain a constant total gas flow rate when the partial pressure of propane or oxygen was adjusted separately. For Cu2+ control experiment, a 3 m-long polypropylene tube rather than Cu microtube was used as the reactor with 0.2 M CuSO4 and 0.5 M H2SO4 in the liquid flow. The concentration of Cu2+ was chosen to match the final concentration of Cu2+ after propane activation at 10 mL min−1 gas flow rate and 0.2 mL min−1 liquid flow rate with C3H8 to O2 ratio of 3:1. For temperature dependence experiments, Cu microtube was immersed in water with preset temperatures. A polypropylene tube with 3 m length connected to the inlet of Cu microtube was also placed in water in order to sufficiently preheat the gas-liquid Taylor flow. 1 m length of Cu microtube was used in order to avoid high O2 conversion at elevated temperatures.
Product quantification
The collected gas components were quantified by gas chromatograph (Agilent 7890B) every 30 minutes. The gas chromatography analyses were averaged during a 70-min experiment. The gas chromatograph was equipped with a ShinCarbon ST Micropacked column and a HayeSep Qcolumn. Ar was used as the carrier gas. C3H6, C3H8, CH4, C2H4, CO, CO2 were quantified using a flame ionization detector (FID) with a methanizer, and O2 was quantified using a thermal conductivity detector (TCD). The response factors for these species were calibrated by analyzing a series of standard gas mixtures.
The liquid components were quantified by using a Bruker AVIII 600 MHz NMR spectrometer. Before sampling, Cu2+ ions in the postreaction solutions were firstly removed via electrodeposition to avoid interference on NMR signals due to their paramagnetism61. The NMR sample was prepared by mixing 500 µL of the processed solution with 100 µL of D2O (Sigma-Aldrich, 99.9 atom % D) and 0.05 mM dimethyl sulfoxide (DMSO, Alfa Aesar, ≥99.9%) as internal standard. Acetate anion standard solution (Aladdin, 0.1 mg·mL−1) was used to calibrate the concentration of DMSO. The 1H spectrum was measured with water suppression by using the excitation sculpting method.
The production rate of gaseous product i was calculated as the following equation. QG is the gas flow at the outlet; xi is the molar fraction of product i of the gas flow at the outlet determined by GC; Vm represents molar volume of gas at room temperature (24.5 L mol−1); S is the inner surface area of Cu microtube.
The production rate of liquid product i was calculated as the following equation. QL is the gas flow rate and liquid flow rate at the outlet; ci is the molar concentration of product i in the liquid flow at the outlet, which was determined by NMR; S is the inner surface area of Cu microtube.
The selectivity of product i is based on carbon atoms and was calculated using the following equation:
The conversion of propane and O2 can be calculated as follows, where A stands for the amount of substance.
The concentrations of remaining H2SO4 and formed Cu2+ were calculated from the O2 consumption in Cu dissolution based on the stoichiometric reaction as follows:
The O2 consumption in Cu dissolution can be calculated by using total consumption of O2 minus the the amount of O2 comsumed in propane activation, which can be calculated from the amount of products according to the reaction equation of C3H8 and O2 toward corresponding products.
The concentration of Cu2+ in the postreaction solutions was also analysed using a UV-Vis spectroscopy (Cary 4000 UV-Vis spectrophotometer). The working curve was obtained by analyzing a series standard Cu2+ sample solutions. The measured Cu2+ concentration from UV-Vis was verified with the result obtained based on Eq. (6) within a difference of less than 4%.
Computational details
Cu2O was selected as the model surface for DFT calculation in this reaction framework, which was justified by the fact that a thin Cu2O layer readily forms on Cu surfaces upon contact with O2 molecules as evidenced by both experimental and theoretical investigations reported in literature26,59,60. We used a slab (3 × 3) consisting of 3 layers of Cu2O(111) with the bottom layer fixed in its bulk position to simulate the Cu surface. The projector augmented wave (PAW) method was used to calculated the interaction between atomic cores and valence electrons as implemented in Vienna ab initio Simulation Package (VASP)62,63,64. The Perdew-Burke-Ernzerhof (PBE) functional65 was used to treat the exchange-correlation interaction. The plane-wave cut off was set to 400 eV. The semi-empirical D3 approach was employed to describe London dispersion interactions as implemented in spin-polarized VASP. To avoid interactions between successive slabs due to the periodic boundary conditions, a vacuum of 50 Å was introduced to the supercell. The reciprocal space was sampled by using a Monkhorst-Pack k-point mesh of 4 × 4 × 166. Each calculation is considered as converged if the electronic energy between two self-consistency steps is smaller than 10−4 eV. We applied the approach proposed by Head-Gordon et al. and Goddard et al67,68,69 to simulate the charged surface interacting with the solvent. In this approach, the linear Poisson-Boltzmann implicit solvation model with a Debye screening length of 3.0 Å was used to neutralize the non-zero charge in the simulation cell and to simulate water and electrolyte, allowing for a more realistic description of the electrical double layer.
The free energies of the slab systems were calculated as follows:
where \({E}_{{{{{{\rm{elec}}}}}}}^{{{{{{\rm{solv}}}}}}}\) is the electronic energy of the system calculated from VASP. We treated all degrees of freedom of the adsorbates as vibrational and neglect the contribution of vibrations of the slab. The finite difference method was used to evaluate the vibrational frequencies (ν) by calculating the partial Hessian matrix. To avoid unphysically large entropy contributions, unusually low vibrational modes (<50 cm−1) were corrected to 50 cm−1. The zero-point vibrational energy (ZPVE), vibrational contributions to the internal energy (Hvib) and entropy (Svib) at 298 K were calculated as follows:
The free energies of small molecules were determined as follows:
where n is 5 for linear molecules and 6 for non-linear molecules. ZPVE was calculated as shown above. Hvib, Svib, Strans, and Srot were obtained from Jaguar by using the PBE/6-31 G* basis set. The free energy of H+ was estimated from the pKa of H3O+ and the calculated free energies of H3O+ and H2O using the solvation model. Detailed descriptions of this approach has been provided in our previous works70,71,72,73,74.
The transition state of each reaction was firstly approached using the nudged elastic band (NEB) method75. The plane-wave cutoff, functional, smearing parameter, and calculator parameters were the same as those used in slab geometry optimizations. Structures obtained from NEB were employed to generate the input structure and orientation for the dimer calculation76. The force of the dimer calculation was converged to <0.1 eV Å−1 to locate the saddle point accurately, i.e., the transition state, which were further verified with the vibrational frequency analysis. The reaction free energy is chosen as the free energy barrier when the calculated free energy barrier is smaller than the corresponding reaction free energy or zero.
Data availability
The data that support the findings of this study are available from the corresponding author upon request. Source data are provided with this paper.
References
Sattler, J. J., Ruiz-Martinez, J., Santillan-Jimenez, E. & Weckhuysen, B. M. Catalytic dehydrogenation of light alkanes on metals and metal oxides. Chem. Rev. 114, 10613–10653 (2014).
Corma, A., Melo, F. V., Sauvanaud, L. & Ortega, F. Light cracked naphtha processing: controlling chemistry for maximum propylene production. Catal. Today 107-108, 699–706 (2005).
Ren, T., Patel, M. & Blok, K. Olefins from conventional and heavy feedstocks: energy use in steam cracking and alternative processes. Energy 31, 425–451 (2006).
Carter, J. H. et al. Direct and oxidative dehydrogenation of propane: from catalyst design to industrial application. Green Chem. 23, 9747–9799 (2021).
Chen, S. et al. Propane dehydrogenation: catalyst development, new chemistry, and emerging technologies. Chem. Soc. Rev. 50, 3315–3354 (2021).
Zhao, D. et al. In situ formation of ZnOx species for efficient propane dehydrogenation. Nature 599, 234–238 (2021).
Motagamwala, A. H., Almallahi, R., Wortman, J., Igenegbai, V. O. & Linic, S. Stable and selective catalysts for propane dehydrogenation operating at thermodynamic limit. Science 373, 217–222 (2021).
Qi, L. et al. Propane Dehydrogenation Catalyzed by Isolated Pt Atoms in identical with SiOZn-OH Nests in Dealuminated Zeolite Beta. J. Am. Chem. Soc. 143, 21364–21378 (2021).
Gambo, Y. et al. Catalyst design and tuning for oxidative dehydrogenation of propane – A review. Appl. Catal. A: Gen. 609, 117914 (2021).
Gao, X. et al. Dimensional Understanding of Boron-Based Catalysts for Oxidative Propane Dehydrogenation: Structure and Mechanism. ACS Catal 13, 9667–9687 (2023).
Jiang, X. et al. Oxidative Dehydrogenation of Propane to Propylene with Soft Oxidants via Heterogeneous Catalysis. ACS Catal 11, 2182–2234 (2021).
Barman, S. et al. Single-Site VOx moieties generated on silica by surface organometallic chemistry: a way to enhance the catalytic activity in the oxidative dehydrogenation of propane. ACS Catal. 6, 5908–5921 (2016).
You, R. et al. NbOx /CeO2 -rods catalysts for oxidative dehydrogenation of propane: Nb–CeO2 interaction and reaction mechanism. J. Catal. 348, 189–199 (2017).
Otroshchenko, T. et al. Current status and perspectives in oxidative, non-oxidative and CO2-mediated dehydrogenation of propane and isobutane over metal oxide catalysts. Chem. Soc. Rev. 50, 473–527 (2021).
Zhou, H. et al. Isolated boron in zeolite for oxidative dehydrogenation of propane. Science 372, 76–80 (2021).
Jiang, X. et al. Recent advances in oxidative dehydrogenation of propane to propylene on boron-based catalysts. Catal. Rev. 1–80 (2022).
Grant, J. T. et al. Selective oxidative dehydrogenation of propane to propene using boron nitride catalysts. Science 354, 1570–1573 (2016).
Liu, Z. et al. Plasma tuning local environment of hexagonal boron nitride for oxidative dehydrogenation of propane. Angew. Chem. Int. Ed 60, 19691–19695 (2021).
Tian, H., Liu, Y. & Xu, B. Kinetic investigations of oxidative dehydrogenation of propane on boron oxide in confined spaces. Catal. Today 420, 114048 (2023).
Cao, L. et al. Antiexfoliating h-BN superset In2O3 catalyst for oxidative dehydrogenation of propane in a high-temperature and water-rich. Environment. J. Am. Chem. Soc. 145, 6184–6193 (2023).
Lu, W.-D. et al. Supported boron oxide catalysts for selective and low-temperature oxidative dehydrogenation of propane. ACS Catal 9, 8263–8270 (2019).
Zhang, X. et al. Radical chemistry and reaction mechanisms of propane oxidative dehydrogenation over hexagonal boron nitride. Catalysts. Angew. Chem. Int. Ed. 59, 8042–8046 (2020).
Zhang, Z. et al. Unraveling radical and oxygenate routes in the oxidative dehydrogenation of propane over boron nitride. J. Am. Chem. Soc. 145, 7910–7917 (2023).
Gao, X. et al. Subsurface nickel boosts the low-temperature performance of a boron oxide overlayer in propane oxidative dehydrogenation. Nat. Commun. 14, 1478 (2023).
Venegas, J. M., McDermott, W. P. & Hermans, I. Serendipity in catalysis research: boron-based materials for alkane oxidative dehydrogenation. Acc. Chem. Res. 51, 2556–2564 (2018).
Zhang, H. et al. Activation of light alkanes at room temperature and ambient pressure. Nat. Catal. 6, 666–675 (2023).
Santos, A. et al. Direct synthesis of hydrogen peroxide over Au–Pd supported nanoparticles under ambient conditions. Ind. Eng. Chem. Res. 58, 12623–12631 (2019).
Landon, P., Collier, P. J., Papworth, A. J., Kiely, C. J. & Hutchings, G. J. Direct formation of hydrogen peroxide from H2/O2 using a gold catalyst. Chem. Commun., 2058-2059 (2002).
Huang, X. et al. Au-Pd separation enhances bimetallic catalysis of alcohol oxidation. Nature 603, 271–275 (2022).
Jiang, X., Zhang, J. & Ma, S. Iron catalysis for room-temperature aerobic oxidation of alcohols to carboxylic acids. J. Am. Chem. Soc. 138, 8344–8347 (2016).
Chen, B., Wang, L. & Gao, S. Recent advances in aerobic oxidation of alcohols and amines to imines. ACS Catal. 5, 5851–5876 (2015).
Nitopi, S. et al. Progress and perspectives of electrochemical CO2 reduction on copper in aqueous electrolyte. Chem Rev 119, 7610–7672 (2019).
Bagemihl, I., Bhatraju, C., van Ommen, J. R. & van Steijn, V. Electrochemical Reduction of CO2 in Tubular Flow Cells under Gas-Liquid Taylor Flow. ACS Sustain. Chem. Eng. 10, 12580–12587 (2022).
Li, C., Xiong, H., He, M., Xu, B. & Lu, Q. Oxyhydroxide Species Enhances CO2 Electroreduction to CO on Ag via Coelectrolysis with O2. ACS Catal. 11, 12029–12037 (2021).
Thorarinsdottir, A. E., Erdosy, D. P., Costentin, C., Mason, J. A. & Nocera, D. G. Enhanced activity for the oxygen reduction reaction in microporous water. Nat. Catal. 6, 425–434 (2023).
Wang, T. et al. Enhancing oxygen reduction electrocatalysis by tuning interfacial hydrogen bonds. Nat. Catal. 4, 753–762 (2021).
Sievers, G. W. et al. Self-supported Pt-CoO networks combining high specific activity with high surface area for oxygen reduction. Nat. Mater. 20, 208–213 (2021).
Han, S. et al. Ultralow overpotential nitrate reduction to ammonia via a three-step relay mechanism. Nat. Catal. 6, 402–414 (2023).
Singh, A. R. et al. Electrochemical Ammonia Synthesis—The Selectivity Challenge. ACS Catal. 7, 706–709 (2016).
Sheng, L., Chen, Y., Deng, J. & Luo, G. High‐frequency formation of bubble with short length in a capillary embedded step T‐junction microdevice. AlChE J. 67, e17376 (2021).
Sheng, L., Chen, Y., Wang, K., Deng, J. & Luo, G. General rules of bubble formation in viscous liquids in a modified step T-junction microdevice. Chem. Eng. Sci. 239, 116621 (2021).
Kreutzer, M. T., Kapteijn, F., Moulijn, J. A. & Heiszwolf, J. J. Multiphase monolith reactors: chemical reaction engineering of segmented flow in microchannels. Chem. Eng. Sci. 60, 5895–5916 (2005).
Sobieszuk, P., Aubin, J. & Pohorecki, R. Hydrodynamics and mass transfer in gas-liquid flows in microreactors. Chem. Eng. Technol. 35, 1346–1358 (2012).
Yin, Y. et al. Dynamics and mass transfer characteristics of CO2 absorption into MEA/[Bmim][BF4] aqueous solutions in a microchannel. Sep. Purif. Technol. 210, 541–552 (2019).
Dietrich, N., Loubière, K., Jimenez, M., Hébrard, G. & Gourdon, C. A new direct technique for visualizing and measuring gas–liquid mass transfer around bubbles moving in a straight millimetric square channel. Chem. Eng. Sci. 100, 172–182 (2013).
Kobayashi, J. et al. A microfluidic device for conducting gas-liquid-solid hydrogenation reactions. Science 304, 1305–1308 (2004).
Sheng, L., Chang, Y., Wang, J., Deng, J. & Luo, G. Remarkable improvement of gas–liquid mass transfer by modifying the structure of conventional T‐junction microchannel. AlChE J. 69, e18089 (2023).
Yan, H. et al. Identifying boron active sites for the oxidative dehydrogenation of propane. ACS Catal. 11, 9370–9376 (2021).
Jiang, X. et al. Multiple promotional effects of vanadium oxide on boron nitride for oxidative dehydrogenation of propane. JACS Au 2, 1096–1104 (2022).
Li, P. et al. Engineering O-O species in boron nitrous nanotubes increases olefins for propane oxidative dehydrogenation. J. Am. Chem. Soc. 144, 5930–5936 (2022).
Ma, F., Chen, S., Wang, Y., Chen, F. & Lu, W. Characterization of redox and acid properties of mesoporous Cr–TiO2 and its efficient performance for oxidative dehydrogenation of propane. Appl. Catal. A: Gen. 427-428, 145–154 (2012).
Xie, Q. et al. Oxidative dehydrogenation of propane to propylene in the presence of HCl Catalyzed by CeO2 and NiO-modified CeO2 nanocrystals. ACS Catal. 8, 4902–4916 (2018).
Barbero, B. Molybdenum role: Mo-Sm-V-O catalytic system for propane oxidative dehydrogenation. Appl. Catal., A: Gen. 252, 133–147 (2003).
Chen, S. et al. Modulating lattice oxygen in dual-functional Mo-V-O mixed oxides for chemical looping oxidative dehydrogenation. J. Am. Chem. Soc. 141, 18653–18657 (2019).
Cao, L. et al. Spherical superstructure of boron nitride nanosheets derived from boron-containing metal-organic frameworks. J. Am. Chem. Soc. 142, 8755–8762 (2020).
Michorczyk, P., Kuśtrowski, P., Niebrzydowska, P. & Wach, A. Catalytic performance of sucrose-derived CMK-3 in oxidative dehydrogenation of propane to propene. Appl. Catal. A: Gen. 445–446, 321–328 (2012).
Li, J.-H. et al. Mesoporous nickel oxides as effective catalysts for oxidative dehydrogenation of propane to propene. Appl. Catal., A: Gen. 382, 99–105 (2010).
Ayandiran, A. A. et al. Oxidative dehydrogenation of propane to propylene over VOx/CaO–γ-Al2O3 using lattice oxygen. Catal. Sci. Technol. 6, 5154–5167 (2016).
Chua, F. M., Kuk, Y. & Silverman, P. J. Oxygen chemisorption on Cu(110): an atomic view by scanning tunneling microscopy. Phys. Rev. Lett. 63, 386–389 (1989).
Dubois, L. H. Oxygen chemisorption and cuprous oxide formation on Cu(111): a high resolution EELS study. Surf. Sci. 119, 399–410 (1982).
Narsimhan, K. et al. Methane to acetic acid over Cu-exchanged zeolites: mechanistic insights from a site-specific carbonylation reaction. J. Am. Chem. Soc. 137, 1825–1832 (2015).
Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758–1775 (1999).
Kresse, G. & Hafner, J. Ab initio molecular dynamics for liquid metals. Phys. Rev. B Condens. Matter 47, 558–561 (1993).
Kresse, G. & Hafner, J. Ab initio molecular-dynamics simulation of the liquid-metal-amorphous-semiconductor transition in germanium. Phys. Rev. B Condens. Matter 49, 14251–14269 (1994).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Monkhorst, H. J. & Pack, J. D. Special points for Brillouin-zone integrations. Phys. Rev. B 13, 5188–5192 (1976).
Sundararaman, R. & Goddard, W. A. 3rd. The charge-asymmetric nonlocally determined local-electric (CANDLE) solvation model. J. Chem. Phys. 142, 064107 (2015).
Goodpaster, J. D., Bell, A. T. & Head-Gordon, M. Identification of possible pathways for C-C bond formation during electrochemical reduction of CO2: new theoretical insights from an improved electrochemical model. J. Phys. Chem. Lett. 7, 1471–1477 (2016).
Sundararaman, R., Goddard, W. A. 3rd & Arias, T. A. Grand canonical electronic density-functional theory: algorithms and applications to electrochemistry. J. Chem. Phys. 146, 114104 (2017).
Zhang, H., Goddard, W. A., Lu, Q. & Cheng, M. J. The importance of grand-canonical quantum mechanical methods to describe the effect of electrode potential on the stability of intermediates involved in both electrochemical CO2 reduction and hydrogen evolution. Phys. Chem. Chem. Phys. 20, 2549–2557 (2018).
Zhang, H. et al. Computational and experimental demonstrations of one-pot tandem catalysis for electrochemical carbon dioxide reduction to methane. Nat. Commun. 10, 3340 (2019).
Zhang, H., Li, C., Lu, Q., Cheng, M. J. & Goddard, W. A. Selective activation of propane using intermediates generated during water. Oxidation. J. Am. Chem. Soc. 143, 3967–3974 (2021).
Chang, K., Zhang, H., Chen, J. G., Lu, Q. & Cheng, M.-J. Constant electrode potential quantum mechanical study of CO2 electrochemical reduction catalyzed by N-doped graphene. ACS Catal. 9, 8197–8207 (2019).
Wu, D., Zhang, J., Cheng, M.-J., Lu, Q. & Zhang, H. Machine learning investigation of supplementary adsorbate influence on copper for enhanced electrochemical CO2 reduction performance. J. Phys. Chem. C 125, 15363–15372 (2021).
Henkelman, G. & Jónsson, H. Improved tangent estimate in the nudged elastic band method for finding minimum energy paths and saddle points. J. Chem. Phys. 113, 9978–9985 (2000).
Henkelman, G. & Jónsson, H. A dimer method for finding saddle points on high dimensional potential surfaces using only first derivatives. J. Chem. Phys. 111, 7010–7022 (1999).
Acknowledgements
C.L., H.Z., W.L., and Q.L. acknowledge the financial support from the State Key Laboratory of Chemical Engineering (no. SKL-ChE-23T02). L.S. and G.L. acknowledge the financial support from the National Natural Science Foundation of China (21991104). B.X. acknowledges the financial support from Beijing National Laboratory for Molecular Sciences.
Author information
Authors and Affiliations
Contributions
C.L., G.L., and Q.L. designed the project. C.L. and W.L. performed alkane activation experiments. C.L. and L.S. conducted flow pattern analysis. H.Z. and M.-J.C. performed DFT calculations. B.X. and G.L. contributed to data analysis and discussion. Q.L. supervised the entire project.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks Yejun Guan and the other, anonymous, reviewer for their contribution to the peer review of this work. A peer review file is available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Source data
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Li, C., Zhang, H., Liu, W. et al. Efficient conversion of propane in a microchannel reactor at ambient conditions. Nat Commun 15, 884 (2024). https://doi.org/10.1038/s41467-024-45179-1
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-024-45179-1
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.