Abstract
Tetraphenylethylene (TPE)-based ligands are appealing for constructing metal-organic frameworks (MOFs) with new functions and responsiveness. Here, we report a non-interpenetrated TPE-based scu Zr-MOF with anisotropic flexibility, that is, Zr-TCPE (H4TCPE = 1,1,2,2-tetra(4-carboxylphenyl)ethylene), remaining two anisotropic pockets. The framework flexibility is further anisotropically rigidified by installing linkers individually at specific pockets. By individually installing dicarboxylic acid L1 or L2 at pocket A or B, the framework flexibility along the b-axis or c-axis is rigidified, and the intermolecular or intramolecular motions of organic ligands are restricted, respectively. Synergistically, with dual linker installation, the flexibility is completely rigidified with the restriction of ligand motion, resulting in MOFs with enhanced stability and improved separation ability. Furthermore, in situ observation of the flipping of the phenyl ring and its rigidification process is made by 2H solid-state NMR. The anisotropic rigidification of flexibility in scu Zr-MOFs guides the directional control of ligand motion for designing stimuli-responsive emitting or efficient separation materials.
Similar content being viewed by others
Introduction
Metal-organic frameworks (MOFs) with adjustable porosity and tunable functionality have attracted considerable attention and exhibited enormous potential in various applications1,2,3,4. The structures and properties of MOFs could be topologically designed by judiciously selecting organic ligands and metal components5,6,7. Tetraphenylethylene (TPE)-based ligands with aggregation-induced emission (AIE) characteristics have been widely used in various fields, such as organic light-emitting diodes, photodynamic therapy agents, chemo- and bio-sensors8,9,10,11. The emission of TPE-based ligands is greatly correlated with intramolecular motion and intermolecular stacking states12,13. Such unique optical properties of these ligands provide the opportunity for constructing stimuli-responsive MOFs with new functions14,15,16,17,18,19.
The Zr6 cluster has been widely used to construct stable MOFs due to its tunable connectivity20,21,22,23. Up to now, some TPE-based Zr-MOFs with different topologies, such as ftw, csq, and scu, have been reported24,25,26,27,28,29. As to the TPE-based Zr-MOFs with ftw topology24,28, although the phenyl flipping of organic ligands exists, the organic ligands are firmly and identically immobilized into the framework along a, b, and c directions, and the framework is rigid (Fig. 1). In the csq topology25, the conformation of organic ligands changes accordingly as the framework shrinks or expands in a one-dimensional (1-D) direction along the c-axis, while the stacking state of organic ligands on the ab plane changes insignificantly (Fig. 1). Comparatively, the Zr-MOFs with scu topology, possessing one-dimensional channels, have the potential to separately display the intramolecular motion and intermolecular stacking of organic ligands in a three-dimensional (3-D) anisotropic manner. On the one hand, the variation of the framework along the channel direction is closely related to the intramolecular motion of organic ligands. On the other hand, the change of framework in the a or b directions perpendicular to the channel will affect the intermolecular stacking state of ligands (Fig. 1). Thus, constructing the anisotropically flexible TPE-based Zr-MOFs with scu topology is a feasible approach to directionally investigate the intermolecular and intramolecular motions of organic ligands. The scu Zr-MOF (LIFM-114) constructed with ETTC ligand has been synthesized with a 2-fold interpenetrated structure, which made it complex to analyze the different motions of organic ligands27. Although, very recently, a non-interpenetrated scu Zr-MOF has been reported, the inter- and intramolecular motions of organic ligands have yet not been investigated29.
The exploration of directional intermolecular and intramolecular motion requires the anisotropic control of framework flexibility. Linker installation has been reported as an efficient strategy to rigidify the framework flexibility by inserting secondary linkers into a specific position of pristine MOFs30,31,32,33,34,35,36,37,38. For Zr-MOFs with scu topology, there are two types of vacant coordination pockets available for linker installation. Thus, it is possible to control the anisotropic flexibility of scu MOFs by installing different second linkers at different positions. However, previous studies only reported the enhancement of the framework stability through linker installation by connecting the two scu interpenetrated frameworks26. The directional control of intermolecular and intramolecular motion of TPE-based ligands in the non-interpenetrated flexible MOFs has not yet been studied.
Here, we reported an anisotropically flexible non-interpenetrated TPE-based Zr-MOF with scu topology. Through deliberately installing linkers along or perpendicular to the channel direction of scu MOFs, anisotropic framework flexibility was rigidified, and the intermolecular or intramolecular changes of TPE-based ligands were studied separately. In specific, the TPE-based ligand, 1,1,2,2-tetra(4-carboxylphenyl)ethylene (H4TCPE), was selected to construct the MOF, Zr-TCPE (Fig. 2a). The simulation of HOMO-LUMO plots demonstrated the molecular orbitals upon the conformational changes of Zr-TCPE. According to size matching, different linear linkers, naphthalenedicarboxylic acid (L1) and fumaric acid (L2), were selected to install into Zr-TCPE at vacant coordination pocket A and pocket B, respectively, further to rigidify the anisotropic flexibility of Zr-TCPE. The 2H solid-state NMR spectra (SSNMR) showed the in situ flipping of phenyl rings of TCPE ligands in Zr-TCPE and its rigidification in Zr-TCPE-L1. Besides, the fluorescence spectra of Zr-TCPE before and after linker installation illustrated the role of intermolecular and intramolecular motions. On the one hand, the decrease of the spacing of pocket A resulted in the close intermolecular stacking of TCPE ligands. The installation of L1 at pocket A rigidified the flexibility of Zr-TCPE on the ab plane. On the other hand, the linker installation at pocket B rigidified the flexibility of Zr-TCPE along the c-axis and restricted the intramolecular motion of TCPE ligands, resulting in enhanced chemical stability and fluorescent stability. Finally, the rigidified TPE-based Zr-MOFs with scu topology showed good separation efficiency for isomers. The elucidation of the inter-/intramolecular motions of TPE-based ligands and the flexibility rigidification of Zr-MOFs with scu topology paves the road to designing highly efficient emitter and separator.
Results and discussion
Characterizations of Zr-TCPE
Zr-TCPE was solvothermally synthesized by reacting ZrCl4 and H4TCPE in N, N’-dimethylformamide (DMF) solution at 120 °C with acetic acid (AA) and water as modulators (Fig. 2)39,40. Due to the flexibility of the organic ligand and the fast nucleation between the Zr and this organic ligand, large-sized single crystals of Zr-TCPE were hard to obtain, although extensive attempts had been conducted. Thus, the powder X-ray diffraction (PXRD) Rietveld refinement was utilized to reveal the structure of this material (Supplementary Fig. 1)29. The refinement results indicated that Zr-TCPE crystallizes in orthorhombic crystal system with Cmmm space group. The diffraction peaks at 5.85°, 7.29°, 9.35°, 10.13°, 11.72°, and 12.49° represented the (020), (001), (021), (130), (040), and (130) planes in Zr-TCPE, respectively (Supplementary Table 3). Detailed crystallographic parameters, atomic positions, and diffraction parameters were given in Supplementary Information (Supplementary Tables 1–3). The crystallographic parameters were slightly different from the reported scu TPE-based MOFs29. Each TCPE4- ligand was connected to four Zr6 clusters, while each Zr6 cluster was coordinated with eight TCPE4− ligands, generating a non-interpenetrated scu structure. The unsaturated metal sites were occupied by terminal H2O or OH− groups and acetate. The Zr-TCPE exhibited scu topology with a fence shape, generating rhombic channels of 9.3 × 23.0 Å along the [001] direction and 5.2 × 11.7 Å along the [100] direction (Supplementary Figs. 2–4). There were two vacant coordination pockets of different sizes in Zr-TCPE, namely, pocket A and pocket B (Fig. 2a).
The non-interpenetrated structure of Zr-TCPE was further confirmed by low-dose high-resolution transmission electron microscopy (HRTEM) imaging (Fig. 2)41,42,43. The low electron dose (only a few electrons per square angstrom) of HRTEM avoids the structural damage of Zr-TCPE under electron beams. The black dots in the HRTEM images represented the Zr6 clusters. The fast Fourier transform (FFT) pattern of the marked area in the HRTEM image was acquired. The calculated d-spacing of (020), (001), and (021) was 1.53 nm, 1.26 nm, and 0.95 nm, respectively, which was consistent with the d-spacing from PXRD refinement (Fig. 2c and Supplementary Table 3). For better interpretation, the raw image was processed by correcting the effect of the contrast transfer function (CTF) of the objective lens (Supplementary Fig. 5). Furthermore, the simulated electron diffraction (ED) pattern along the [100] direction was consistent with the selected area electron diffraction (SAED) pattern of the HRTEM image (Supplementary Fig. 6). The average background subtraction filter (ABSF)-filtered CTF-corrected image in Fig. 2d matched well with the simulated structure of Zr-TCPE along the [100] direction zone axis (Supplementary Fig. 3). The distances between two adjacent Zr6 clusters were measured from the linear profiling along the b- and c-axis as 1.53 nm and 1.23 nm, respectively (Supplementary Fig. 7), which were consistent with the simulated structure of Zr-TCPE (Supplementary Fig. 3). Besides, the distance of Zr6 clusters along the c-axis was comparable to the c-axis cell parameter in non-interpenetrated Zr-TCPE. Thus, not interpenetrated but non-interpenetrated structure was assigned to Zr-TCPE. We also obtained diffraction information of (020) and (130) planes from the FFT images (Supplementary Fig. 8). All the above results verified the non-interpenetrated structure of Zr-TCPE.
The high-angle annular dark-field (HAADF) images of Zr-TCPE were also collected to further character the diffraction information (Supplementary Figs. 9 and 10). The denoised image and FFT pattern were also acquired. The white dots in these images represented the Zr6 clusters. The calculated d-spacing of the (020) plane was 1.54 nm, which was comparable to d = 1.51 nm from XRD refinement. Besides, as shown in Supplementary Fig. 10, the distance between two adjacent Zr6 clusters was calculated from the linear profiling in two directions. Due to the limitation of resolution, the distance between two adjacent Zr6 clusters along the b-axis was hard to observe directly because of the interference from Zr6 clusters along the a-axis. Thus, the denoised images were acquired by an inverse-FFT process after applying a periodic mask to the FFT pattern for measuring the distance of Zr6 clusters. The measured distance of adjacent Zr6 clusters was around 1.79 nm and 3.04 nm (Supplementary Fig. 10). These values were consistent with the simulated value along the a-axis and b-axis, respectively, in a non-interpenetrated structure but differed from the distance of adjacent Zr6 clusters in a double-interpenetrated structure (0.89 nm and 1.51 nm, see Supplementary Figs. 3 and 4). The results further proved that the Zr-TCPE possessed a non-interpenetrated structure.
The synthesized Zr-TCPE exhibited a wool ball shape with an average size of about 100 nm (Supplementary Fig. 11). The 1H NMR result of the digested Zr-TCPE confirmed the existence of TCPE ligands, DMF solvents, and acetic acid in the framework (Supplementary Fig. 12). To accurately characterize the porosity of Zr-TCPE, both the N2 and Ar adsorption-desorption isotherms were performed at 77 K and 87 K, respectively. As shown in Supplementary Fig. 13, both the isotherms presented fully reversible type-I behavior, indicating the microporous characteristic of Zr-TCPE. The Brunauer-Emmett-Teller (BET) surface area, pore size distribution, and total pore volume obtained from the Ar adsorption isotherms are consistent with those from N2 adsorption isotherms (Supplementary Table 4). The main pore size of Zr-TCPE calculated by the DFT method from Ar and N2 sorption isotherms was 8.7 Å and 9.4 Å, respectively. The calculated pore size was comparable to the simulated size of pocket A in Zr-TCPE (9.3 Å), indicating the non-interpenetrated feature of Zr-TCPE.
Anisotropic flexibility of Zr-TCPE
The conformation changes of TPE-based ligands in response to external stimuli bring flexibility to MOFs. This flexibility could be reflected in the variation of emission properties of MOFs, which is usually correlated with AIE characteristics of TPE-based ligands27,44,45. Thus, we tested the emission properties of Zr-TCPE under the external stimuli of temperature. Under different heating temperatures of 200, 220, and 250 °C, the fluorescence emission of Zr-TCPE red-shifted from 460 nm to 470 nm and 517 nm, respectively (Fig. 3d and Supplementary Fig. 14). After heating Zr-TCPE under 250 °C (Zr-TCPE-H), the color of Zr-TCPE changed from white to yellow (Supplementary Fig. 15a). Meanwhile, the photoluminescent color changed from blue to light green under the 365 nm excitation (Supplementary Fig. 15b). It has been reported that the color change and the fluorescence red-shift of TPE-based MOFs resulted from the intramolecular motion and close stacking of TPE ligands27,45. In the case of Zr-TCPE, the motion and stacking changes were caused by the loss of solvent molecules and coordinated modulators in vacant coordination pockets, which was evidenced by the 1H-NMR of digested Zr-TCPE-H (Supplementary Fig. 16). The intramolecular motion of TCPE ligands in Zr-TCPE was associated with the framework change along the c-axis, indicating the framework flexibility along the c-axis. The close stacking of TCPE ligands in Zr-TCPE corresponded to the framework change on the ab plane (Supplementary Fig. 3). To demonstrate the conformational change and electric states of organic ligands, DFT calculations were performed on H4TCPE ligands in Zr-TCPE and Zr-TCPE-H, respectively. The ligand exhibited a more twisted conformation in Zr-TCPE-H. Besides, the energy gap between the HOMO and LUMO was 2.684 eV for Zr-TCPE, while it was 2.284 eV for Zr-TCPE-H (Fig. 3a). The decreased energy gap resulted in lower emission energy for Zr-TCPE-H, which was consistent with the fluorescence results.
To further investigate the structural change, the PXRD patterns, HAADF images, Raman spectra, transmission electron microscopy (TEM), and scanning electron microscopy (SEM) images of Zr-TCPE-H were collected. The PXRD patterns showed that the first diffraction peaks of the heated Zr-TCPE shifted to a smaller degree (Fig. 3c), indicating the increase of interplanar spacing of the (020) plane. The HAADF images of Zr-TCPE-H also proved that the d value of the (020) plane increased from 1.54 nm to 1.65 nm (Fig. 3b and Supplementary Fig. 17). Besides, the measured distance of adjacent Zr6 clusters along the b-axis had also increased from 3.04 nm to 3.25 nm (Supplementary Fig. 18). All the results demonstrated the framework change along the b-axis after heating treatment, indicating the framework flexibility along the b-axis. It was worth noting that the measured distance of adjacent Zr6 clusters along the a-axis displayed no significant changes possibly due to the technical resolution limitation (Supplementary Fig. 18). In addition, the main pore size of Zr-TCPE-H was 6.8 Å, smaller than that of Zr-TCPE (Supplementary Fig. 19). The reduced pore size proved the shrinkage along the a-axis, indicating the framework flexibility along the a-axis. The above experiments and characterizations demonstrated the anisotropic flexibility of Zr-TCPE (Fig. 3e). These phenomena illustrated the transformation from Zr-TCPE to Zr-TCPE-H. The SEM and TEM images of Zr-TCPE-H still displayed the original morphology, which excluded the possibility of framework collapse (Supplementary Fig. 20). The Raman peak at 412 cm−1 was assigned to the stretching modes of Zr-O (carboxylate), and the peak at 1125 cm−1 was related to the stretching vibration of the C-C bond formed between ethylene and phenyl ring (Supplementary Fig. 21). Another obvious Raman peak at 1607 cm−1 was assigned to the stretching vibration of the C = C band from phenyl rings and ethylene core45,46,47. Compared with Zr-TCPE, neither Raman peaks disappeared nor new Raman peaks appeared in Zr-TCPE-H, indicating unchanged chemical composition in Zr-TCPE after heating45,46. To explore whether this transformation is reversible, another external stimulus is needed to restore the original structure. Then, these heated materials were treated in DMF solution with acetic acid under different temperatures for 12 h (see Supplementary Information for details). The use of temperature is important to restore the structure. At 100 °C or 120 °C, the PXRD patterns and fluorescence emission were completely restored with the addition of acetic acid (Fig. 3d and Supplementary Figs. 22–24). These results proved the reversible transformation of Zr-TCPE, further proving the anisotropic flexibility of Zr-TCPE.
Anisotropic rigidification of flexibility in Zr-TCPE
To directionally control the anisotropic flexibility of Zr-TCPE, we employed the linker installation strategy. In the scu topology of Zr-TCPE, each Zr6 cluster was coordinated with eight TCPE4− ligands, leaving two types of vacant coordination pockets, packet A along the c-axis and pocket B along the a-axis (Fig. 2a). The space of pocket A is about 9.3 Å, which is almost equal to the length of naphthalenedicarboxylic acid (L1, 9.1 Å). Meanwhile, the space of pocket B (5.2 Å) is similar to the length of fumaric acid (L2, 4.9 Å). Thus, by post-synthetic modification, L1 and L2 could coordinate on the unsaturated metal sites in pocket A and pocket B, respectively (Fig. 4). This strategy allowed the precise control of anisotropic flexibility in Zr-TCPE and separately investigated the TPE motions along different directions. Through soaking fresh Zr-TCPE in DMF solution of the excessive amounts of installed linkers at 75 °C for 24 h under stirring, Zr-TCPE-L1 and Zr-TCPE-L2 were synthesized. Meanwhile, with the dual linker installation (DLI), the Zr-TCPE-DLI was also obtained, in which the installation order is installing L2 first and then L1.
To quantitatively analyze the installed linkers, the 1H NMR spectra of the digested materials after installation were measured, proving the successful introduction of the two linkers (Supplementary Figs. 25–34). The ratios of the installed linkers to the original ligands in the Zr-TCPE series were calculated (Supplementary Table 5). Ideally, if the vacant coordination pockets in Zr-TCPE are fully occupied with installed linkers, the ligand ratio of L1: L2: TCPE will be 0.5: 0.5: 1. In Zr-TCPE-L1, the ratio of L1 to TCPE was 0.5: 1, which was consisted with the theoretical value. Because of the size mismatching between the space of pocket B and the length of L1, the possibility of L1 coordinated on pocket B was ruled out. Thus, pocket A was fully occupied by L1 in Zr-TCPE-L1. The ratio of L2 to TCPE was 0.4:1, which was smaller than the theoretical ratio. It resulted from the steric hindrance of pocket B in the original MOF that prevented full coordination at pocket B. Meanwhile, L2 was small enough to coordinate at pocket A as the dangling linker. Thus, L2 was partially coordinated on both pocket A and B. The ligand ratio of L1: L2: TCPE in Zr-TCPE-DLI was 0.5: 0.1: 1. Considering that L1 could only coordinate on pocket A, while L2 possessed the ability to coordinate on pocket A and B, the 1H NMR results of the sequential experiments (L2-L1) illustrated that the L2 first dangled at pocket A was then replaced by L1, leading to the full coordination of L1 at pocket A. We also reversed the insertion sequence (L1-L2), and the ligand ratio of L1: L2: TCPE was calculated as 0.3: 0.3: 1 (see Supplementary Information for details). Besides, the 1H NMR of the above MOFs after thermal treatment under 250 °C for 6 h and digestion were measured. For all MOFs after thermal treatment, the ratios of additional linkers to TCPE almost remained the same, exhibiting that the installed linkers are thermally stable under 250 °C (Supplementary Table 5).
Further, the PXRD patterns, SEM, and TEM images of Zr-TCPE-L1, Zr-TCPE-L2, and Zr-TCPE-DLI indicated that the linker installation process did not change the structure and morphology of the original MOF (Supplementary Figs. 35 and 36). The PXRD patterns of Zr-TCPE-DLI immersing in aqueous solutions with different pH values exhibited no obvious difference. Besides, the crystallinity of Zr-TCPE-DLI was well maintained after 15 months of storage, which further indicated the enhanced chemical stability (Supplementary Fig. 37). To characterize the porosity parameters of Zr-TCPE after linker installation, N2 adsorption-desorption isotherms were performed at 77 K. As shown in Supplementary Fig. 38, all the isotherms exhibited reversible type-I behavior, indicating the existence of micropores in MOFs. The BET surface area of Zr-TCPE-L1 and Zr-TCPE-L2 were 670 m2/g and 894 m2/g, respectively, which were smaller than that of Zr-TCPE. As shown in Supplementary Fig. 38b, the main size of pores in Zr-TCPE-L1 was 6.4 Å, which corresponded to the partitioning of the rhombic pores (9.4 Å) by L1 at pocket A. Due to technical limitations, the pore partition phenomenon of the other rhombic pores (~5.2 Å, calculated from the simulated structure) by L2 at pocket B could not be observed from the N2 adsorption-desorption results. Nevertheless, the major pore size of Zr-TCPE-L2 (8.0 Å) was slightly smaller than that of Zr-TCPE (Supplementary Fig. 38b). It was because L2 possessed the ability to coordinate on the metal sites at pocket A, L2 could partly dangle on pocket A and reduce the pore size.
The successful installation of linkers at different pockets along different axis directions in Zr-TCPE provides the potential to anisotropically rigidify the framework flexibility and separately investigate the TPE intermolecular and intramolecular motions. The fluorescence behaviors of Zr-TCPE-L1, Zr-TCPE-L2, and Zr-TCPE-DLI before and after heating were recorded. Note that these materials were heated at 250 °C for 6 h before characterization, namely Zr-TCPE-L1-H, Zr-TCPE-L2-H, and Zr-TCPE-DLI-H, respectively. As shown in Fig. 5a, the fluorescence emission of Zr-TCPE-L2-H was similar to the original Zr-TCPE-L2. In contrast, the emission of Zr-TCPE-L1-H red-shifted apparently from 460 nm to 490 nm compared with the original Zr-TCPE-L1. The different fluorescence behavior of Zr-TCPE-L1 and Zr-TCPE-L2 was attributed to the different motion states of TCPE ligands in Zr-TCPE. As reported, the fluorescence changes of TPE-based molecules are more dependent on intramolecular motion than intermolecular motion27,45. The installation of L1 at pocket A rigidified the flexibility and restricted the intermolecular stacking between adjacent organic ligands on the ab plane. The intramolecular motion of ligands and the flexibility along the c-axis still existed in Zr-TCPE-L1 due to the vacant pocket B (Fig. 5c), leading to red-shift fluorescence of Zr-TCPE-L1 under heating. On the other hand, the installation of L2 at pocket B was more likely to rigidify the flexibility along the c-axis and restrict the intramolecular motion of organic ligands due to the steric hindrance (Fig. 5d). The intermolecular motion of ligands and the flexibility on the ab plane in Zr-TCPE-L2 had little influence on fluorescence emission. As a result, the fluorescence behavior of Zr-TCPE-L2 exhibited no obvious change after the heating process. Besides, with dual linker installation, the anisotropic flexibility of Zr-TCPE-DLI was completely rigidified (Fig. 5e), which was confirmed by the unchanged fluorescence of Zr-TCPE-DLI. These results indicated that the intermolecular and intramolecular motion of TPE-based ligands can be investigated with the anisotropic rigidification of framework flexibility through linker installation.
To in situ study the intramolecular dynamics, such as the flipping of phenyl ring motion of organic ligands in Zr-TCPE before and after linker installation, we synthesized deuterated H4TCPE-d16 ligands to construct Zr-TCPE and Zr-TCPE-L1 and implemented 2H solid-state NMR (2H SSNMR) spectroscopy48,49. The detailed synthesis process and characterization of deuterated H4TCPE-d16 were given in Supplementary Information (Supplementary Figs. 39–47). The PXRD patterns, TEM images, and 1H NMR spectra confirmed the successful synthesis of Zr-TCPE, Zr-TCPE-L1, and Zr-TCPE-L2 constructed with H4TCPE-d16 (Supplementary Figs. 48–51). Variable-temperature 2H SSNMR spectra of Zr-TCPE and Zr-TCPE-L1 were recorded between 300 K and 350 K. As shown in Fig. 5b, the 2H SSNMR spectra of Zr-TCPE and Zr-TCPE-L1 exhibited typical Pake patterns with the splitting of 129 kHz at 300 K, suggesting that the phenyl rings in both samples were almost static. Zr-TCPE at 350 K resulted in a new set of symmetric peaks, while Zr-TCPE-L1 showed almost the same Pake patterns at all temperature ranges. To simulate the 2H SSNMR spectra, a phenyl flipping model was carried out using the EXPRESS package running in MATLAB software. The simulated results displayed the flipping rates of phenyl rings in Zr-TCPE were 1 × 103 Hz, 5 × 103 Hz, and 2.5 × 104 Hz at 300 K, 323 K, and 350 K, respectively. With the temperature increasing, the phenyl rings in Zr-TCPE underwent a faster π-flipping motion, as the typical separating pattern of phenyl flipping (33 kHz) in Zr-TCPE was stronger than that in Zr-TCPE-L1. The slower flipping of phenyl rings in Zr-TCPE-L1 indicated that the installed L1 could block the flipping of the phenyl rings in TCPE. The above results provided a direct tool to in situ observe the flipping of the phenyl ring and its rigidification process.
Isomer separation
It has been reported that the gas chromatographic separation performance was closely related to the size and regularity of pores in MOF-based stationary phases39,50,51,52,53. Thus, to investigate the influence of anisotropic rigidification of flexibility on MOF pores, high-resolution gas chromatography (GC) technique was implemented. Then, Zr-TCPE, Zr-TCPE-L1, Zr-TCPE-L2, Zr-TCPE-DLI, Zr-TCPE-H, Zr-TCPE-L1-H, Zr-TCPE-L2-H, and Zr-TCPE-DLI-H were dynamically coated on the capillary columns as stationary phases for GC separation (Supplementary Fig. 53). It can be seen from the cross-view SEM images of these columns that all the materials were uniformly coated on the inner wall and the coating process did not change the morphology of MOFs (Supplementary Fig. 54). The GC separation on the above MOF columns was feasible due to their thermal stabilities from the thermogravimetric results (Supplementary Fig. 52).
Six groups of isomers, including hexane, octane, nonane, heptene, octene, and ethyltoluene isomers, were employed to evaluate the separation ability of these MOFs (Fig. 6). The Zr-TCPE-H showed seriously low separation ability compared with the original Zr-TCPE (Supplementary Figs. 55 and 56). To further investigate the mechanism of separation differences between Zr-TCPE and Zr-TCPE-H, thermodynamic adsorption and kinetic diffusion experiments were carried out. The adsorption enthalpy (ΔH), adsorption entropy (ΔS), diffusion constant (Ds), and the resistance to mass transfer coefficient (Cs) values were calculated according to van’t Hoff equation and Golay equation, respectively (see the Supplementary Information for detail). The ΔH values for 2-methylpentane were more negative on Zr-TCPE-H coated column than that on Zr-TCPE coated column (Supplementary Fig. 57), indicating the stronger adsorption interactions between the analyte and Zr-TCPE-H54,55. The higher magnitude of ΔS value in the Zr-TCPE-H coated column demonstrated that the analyte had less conformational freedom and was more restricted in Zr-TCPE-H, indicating greater retention55. These differences can be attributed to the different pore sizes of Zr-TCPE (9.4 Å) and Zr-TCPE-H (6.8 Å). Both of the pore sizes were accessible to 2-methylpentane, while the smaller pore size of Zr-TCPE-H led to stronger van der Waals interactions between the analyte and pore walls51. Thus, the Zr-TCPE-H coated column presented higher thermodynamic adsorption to the analyte. The Ds values for 2-methylpentane in Zr-TCPE and Zr-TCPE-H coated columns were 2.02 × 10−12 m2/s and 6.71 × 10−15 m2/s, respectively (Supplementary Fig. 58). The smaller diffusion constant demonstrated a lower diffusion rate for the analyte in Zr-TCPE-H. In addition, the Cs value for 2-methylpentane in Zr-TCPE-H (0.25) was larger than that in Zr-TCPE (7.10 × 10−4). This phenomenon proved the larger mass transfer resistance in Zr-TCPE-H than that in Zr-TCPE39,56. All the above results manifested that the smaller pore size of Zr-TCPE-H induced strong thermodynamic interaction and slow kinetic diffusion, leading to poor separation performance with peak broadening and peak tailing. It was worth noting that the separation performance of Zr-TCPE coated column decreased under the longer heating time, proving the structure change from Zr-TCPE to Zr-TCPE-H (Fig. 6a).
Comparatively, Zr-TCPE-L2-H retained a good separation ability to baseline separate all the isomers without peak tailing compared with Zr-TCPE-L2 (Supplementary Figs. 59 and 60). This phenomenon proved the enhanced stability of Zr-TCPE-L2. The coordination of L2 at pocket B greatly rigidified the flexibility along the c-axis and restricted the intramolecular motion of organic ligands. Meanwhile, the L2 dangled on pocket A restricted the decrease of pores along the a-axis. As a result, the pore size and pore orderliness of Zr-TCPE-L2 were mostly maintained after heating, leading to enhanced separation stability. However, Zr-TCPE-L1-H showed fair separation ability with obvious peak tailing compared with Zr-TCPE-L1 (Supplementary Figs. 61 and 62). Although the installation of L1 at pocket A restricted the intermolecular motion of organic ligands on the ab plane, the intramolecular motion still existed. This intramolecular motion would result in the disordered orientation of phenyl rings in the pore channel, which led to reduced separation ability of Zr-TCPE-L1-H. Note that Zr-TCPE-L1 exhibited much better separation resolution towards ethyltoluene isomers than Zr-TCPE-L2 and Zr-TCPE (Fig. 6b). It came from the smaller pores introduced by the pore partition on pocket A, leading to a more suitable size and shape matching between the pores of MOF and ethyltoluene isomers.
Among all eight MOF columns, Zr-TCPE-DLI demonstrated the best separation resolution for all isomers (Fig. 6, Supplementary Fig. 63, and Supplementary Table 6). Compared with Zr-TCPE, the separation resolution of nonane isomers on the Zr-TCPE-DLI coated column displayed almost no decrease with the extension of heating time, confirming the enhanced separation stability after linker installation (Supplementary Fig. 64). It was worth noting that there was almost no separation efficiency loss in Zr-TCPE-DLI-H (Supplementary Fig. 65), indicating that not only its structural flexibility was completely rigidified but also the pore partition provided suitable pores (Fig. 6). Furthermore, the Zr-TCPE-DLI-H column exhibited identical separation ability towards C8 isomers with eight-times injections (Supplementary Fig. 66), suggesting good column repeatability. Besides, after storage for three months, the Zr-TCPE-DLI-H coated column still showed excellent separation resolution for alkane and alkene isomers, demonstrating improved stability of the Zr-TCPE-DLI (Supplementary Fig. 67). These different separation results further demonstrated the framework flexibility and its rigidification strongly affected and anisotropically tuned the separation properties.
In summary, we synthesized an anisotropically flexible TPE-based Zr-MOF with a non-interpenetrated scu topology. There were two types of vacant coordination pockets inside the framework. The Zr-TCPE exhibited reversible thermofluorochromism behavior due to the anisotropic flexibility. Linker installation was implemented to anisotropically rigidify the framework flexibility. By installing L1 or L2 at pocket A or B, respectively, the flexibility along the b- and c-axis was rigidified correspondingly. Simultaneously, the inter- and intramolecular motion of organic ligands were restricted. The complete rigidification of anisotropic flexibility and ligand motion resulted in enhanced stability and separation performance of Zr-TCPE. The rigidification of anisotropic flexibility guides the investigation of the molecular motions of TPE-based ligands and the construction of stable stationary phases and emitting materials.
Methods
Synthesis of Zr-TCPE
Zr-TCPE was synthesized according to the previous work39. The 10 mg ZrCl4 and 120 μL AA were dissolved in 2 mL DMF in a 4 mL vial. The vial was heated at 100 °C for 1 h. After cooling down to room temperature, 20 μL H2O, 160 μL AA, and 10 mg H4TCPE ligand were added to the mixture. After sonication, the vial was heated at 120 °C for 24 h. The white product was collected by centrifugation and washed with DMF and EtOH three times, respectively, before drying at 60 °C under vacuum.
Synthesis of Zr-TCPE-L1 and Zr-TCPE-L2
The Zr-TCPE-L1 and Zr-TCPE-L2 were synthesized according to the previous report30. Typically, as-synthesized Zr-TCPE (about 15 mg) was soaked in DMF (2 mL) with the addition of the secondary linkers (0.03 M, 4.6 mL DMF). The mixture was stirred at 75 °C for 24 h. The products were collected by centrifugation and soaked in fresh DMF for 3 days to remove uncoordinated linkers.
DFT calculations
The DFT calculations were performed with the DMol3 programs of Materials Studio 19.1.0.2353. The Local Density Approximation (LDA)-PWC functional and DND 3.5 basis were employed for all calculations. During the calculation processes, the default settings embedded in Materials Studio 19.1.0.2353 were used for all calculations. The structural models of H4TCPE ligands were built based on the structures of Zr-TCPE and Zr-TCPE-H, where carboxylates of linkers protonated to balance the charge. To reflect the constraints of the MOF lattice on the conformation of H4TCPE ligands, the carbon atom of the carboxylate group was fixed during the geometry optimization and orbital calculation.
2H solid-state NMR experiments
The experiments were performed on a Bruker 400WB AVANCE III spectrometer at the field of 9.4 T using the solid echo pulse sequence (90°x-τ1-90°y- τ2−acquisition) with scans of 10240. τ1 was set to 150 μs, and τ2 was set to 0 to obtain the complete echo signal. 2H line shape simulations were carried out as a phenyl flipping model using the EXPRESS package running in MATLAB software. The quadrupolar coupling constant CQ and asymmetry parameter η of deuterium was set to 172 kHz and 0.03 according to the Pake patterns under 300 K.
Data availability
The data that support the conclusions of this study are either presented in the paper or its Supplementary Information. The data are available from the corresponding authors upon request. Source data are provided with this paper.
References
Xu, Y., Li, Q., Xue, H. & Pang, H. Metal-organic frameworks for direct electrochemical applications. Coord. Chem. Rev. 376, 292–318 (2018).
Ryu, U. et al. Recent advances in process engineering and upcoming applications of metal-organic frameworks. Coord. Chem. Rev. 426, 213544 (2021).
Qin, Y. et al. Nanostructural engineering of metal-organic frameworks: construction strategies and catalytic applications. Matter 5, 3260–3310 (2022).
Xu, G. et al. Exploring metal organic frameworks for energy storage in batteries and supercapacitors. Mater. Today 20, 191–209 (2017).
Wang, S. et al. Engineering structural dynamics of zirconium metal-organic frameworks based on natural C4 linkers. J. Am. Chem. Soc. 141, 17207–17216 (2019).
Fan, W., Zhang, X., Kang, Z., Liu, X. & Sun, D. Isoreticular chemistry within metal-organic frameworks for gas storage and separation. Coord. Chem. Rev. 443, 213968 (2021).
Kaneti, Y. V. et al. Nanoarchitectured design of porous materials and nanocomposites from metal-organic frameworks. Adv. Mater. 29, 1604898 (2017).
Zhao, Z., Zhang, H., Lam, J. W. Y. & Tang, B. Z. Aggregation-induced emission: new vistas at the aggregate level. Angew. Chem. Int. Ed. Engl. 59, 9888–9907 (2020).
Ma, X. et al. Aggregation-induced emission or aggregation-caused quenching? Impact of covalent bridge between tetraphenylethene and naphthalimide. Chin. Chem. Lett. 32, 1790–1794 (2021).
Balachandran Yekkuni, L. & Jiang, X. Aggregation-induced fluorogens in bio-detection, tumor imaging, and therapy: a review. CCS Chem. 4, 420–436 (2021).
Xu, S., Duan, Y. & Liu, B. Precise molecular design for high-performance luminogens with aggregation-induced emission. Adv. Mater. 32, 1903530 (2020).
Chen, Y., Lam, J. W. Y., Kwok, R. T. K., Liu, B. & Tang, B. Z. Aggregation-induced emission: fundamental understanding and future developments. Mater. Horiz. 6, 428–433 (2019).
Zhu, L., Zhu, B., Luo, J. & Liu, B. Design and property modulation of metal-organic frameworks with aggregation-induced emission. ACS Mater. Lett. 3, 77–89 (2021).
Wu, X.-H. et al. Guest-triggered aggregation-induced emission in silver chalcogenolate cluster metal-organic frameworks. Adv. Sci. 6, 1801304 (2019).
Lustig, W. P. et al. Metal–organic frameworks: functional luminescent and photonic materials for sensing applications. Chem. Soc. Rev. 46, 3242–3285 (2017).
Zhu, B. et al. Cobalt metal-organic frameworks with aggregation-induced emission characteristics for fluorometric/colorimetric dual channel detection of nitrogen-rich heterocyclic compounds. Anal. Chem. 94, 3744–3748 (2022).
Li, Z. et al. Achieving gas pressure-dependent luminescence from an AIEgen-based metal-organic framework. Nat. Commun. 13, 2142 (2022).
Xiong, J., Qian, X., Zhao, L. & Xu, J. A fluorescent responsive tetraphenylethene based metal-organic framework. Inorg. Chem. Commun. 105, 20–25 (2019).
Baroni, N. et al. Inkjet-printed photoluminescent patterns of aggregation-induced-emission chromophores on surface-anchored metal-organic frameworks. ACS Appl. Mater. Interfaces 10, 25754–25762 (2018).
Bai, Y. et al. Zr-based metal-organic frameworks: design, synthesis, structure, and applications. Chem. Soc. Rev. 45, 2327–2367 (2016).
Jia, S. et al. Tuning the connectivity, rigidity, and functionality of two-dimensional Zr-based metal-organic frameworks. Inorg. Chem. 58, 12748–12755 (2019).
Howarth, A. J. et al. Chemical, thermal and mechanical stabilities of metal-organic frameworks. Nat. Rev. Mater. 1, 15018 (2016).
Rimoldi, M. et al. Catalytic zirconium/hafnium-based metal-organic frameworks. ACS Catal. 7, 997–1014 (2017).
Wei, Z. et al. Rigidifying fluorescent linkers by metal-organic framework formation for fluorescence blue shift and quantum yield enhancement. J. Am. Chem. Soc. 136, 8269–8276 (2014).
Zhang, Q. et al. Piezofluorochromic metal-organic framework: a microscissor lift. J. Am. Chem. Soc. 137, 10064–10067 (2015).
Hurlock, M. J. et al. Evolution of 14-connected Zr6 secondary building units through postsynthetic linker incorporation. ACS Appl. Mater. Interfaces 13, 51945–51953 (2021).
Chen, C.-X. et al. All roads lead to rome: tuning the luminescence of a breathing catenated Zr-MOF by programmable multiplexing pathways. Chem. Mater. 31, 5550–5557 (2019).
Li, J. et al. Dumbbell plate-shaped AIEgen-based luminescent MOF with high quantum yield as self-enhanced ECL tags: mechanism insights and biosensing application. Small 18, 2106567 (2022).
Halder, A. et al. Enhancing dynamic spectral diffusion in metal-organic frameworks through defect engineering. J. Am. Chem. Soc. 145, 1072–1082 (2023).
Yuan, S. et al. Linker installation: engineering pore environment with precisely placed functionalities in zirconium MOFs. J. Am. Chem. Soc. 138, 8912–8919 (2016).
Chen, C.-X. et al. Precise modulation of the breathing behavior and pore surface in Zr-MOFs by reversible post-synthetic variable-spacer installation to fine-tune the expansion magnitude and sorption properties. Angew. Chem. Int. Ed. Engl. 55, 9932–9936 (2016).
Chen, C.-X. et al. Dynamic spacer installation for multirole metal-organic frameworks: a new direction toward multifunctional MOFs achieving ultrahigh methane storage working capacity. J. Am. Chem. Soc. 139, 6034–6037 (2017).
Pang, J. et al. Enhancing pore-environment complexity using a trapezoidal linker: toward stepwise assembly of multivariate quinary metal-organic frameworks. J. Am. Chem. Soc. 140, 12328–12332 (2018).
Zhang, X., Frey, B. L., Chen, Y.-S. & Zhang, J. Topology-guided stepwise insertion of three secondary linkers in zirconium metal-organic frameworks. J. Am. Chem. Soc. 140, 7710–7715 (2018).
He, H., Guo, B., Liu, Y., Zhang, L. & Huang, W. Post-synthetic modification of zirconium metal-organic frameworks for adsorption and separation of light hydrocarbons. Cryst. Growth Des. 20, 4882–4885 (2020).
Hong, A. N. et al. Pore-space partition and optimization for propane-selective high-performance propane/propylene separation. ACS Appl. Mater. Interfaces 13, 52160–52166 (2021).
Yang, H. et al. Ultrastable high-connected chromium metal-organic frameworks. J. Am. Chem. Soc. 143, 14470–14474 (2021).
Robison, L. et al. Designing porous materials to resist compression: mechanical reinforcement of a Zr-MOF with structural linkers. Chem. Mater. 32, 3545–3552 (2020).
Xu, M. et al. Homogeneously mixing different metal-organic framework structures in single nanocrystals through forming solid solutions. ACS Cent. Sci. 8, 184–191 (2022).
Sun, S., Wei, C., Xiao, Y., Li, G. & Zhang, J. Zirconium-based metal-organic framework gels for selective luminescence sensing. RSC Adv. 10, 44912–44919 (2020).
Guo, F.-A. et al. Linker vacancy engineering of a robust ftw-type Zr-MOF for hexane isomers separation. Angew. Chem. Int. Ed. Engl. 62, e202303527 (2023).
Liu, L. et al. Imaging defects and their evolution in a metal-organic framework at sub-unit-cell resolution. Nat. Chem. 11, 622–628 (2019).
Liu, G. et al. Eliminating lattice defects in metal-organic framework molecular-sieving membranes. Nat. Mater. 22, 769–776 (2023).
Zhu, Z.-H. et al. Smart tetraphenylethene-based luminescent metal-organic frameworks with amide-assisted thermofluorochromics and piezofluorochromics. Adv. Sci. 9, 2200850 (2022).
Guo, X. et al. Stimuli-responsive luminescent properties of tetraphenylethene-based strontium and cobalt metal-organic frameworks. Angew. Chem. Int. Ed. Engl. 59, 19716–19721 (2020).
Liu, X., Li, A., Xu, W., Ma, Z. & Jia, X. Pressure-induced emission band separation of the hybridized local and charge transfer excited state in a TPE-based crystal. Phys. Chem. Chem. Phys. 20, 13249–13254 (2018).
Gao, Z. et al. Enhanced sensitivity and piezochromic contrast through single-direction extension of molecular structure. Chem. Eur. J. 23, 773–777 (2017).
Shustova, N. B., McCarthy, B. D. & Dincă, M. Turn-on fluorescence in tetraphenylethylene-based metal-organic frameworks: an alternative to aggregation-induced emission. J. Am. Chem. Soc. 133, 20126–20129 (2011).
Shustova, N. B. et al. Phenyl ring dynamics in a tetraphenylethylene-bridged metal-organic framework: implications for the mechanism of aggregation-induced emission. J. Am. Chem. Soc. 134, 15061–15070 (2012).
Chang, N., Gu, Z.-Y. & Yan, X.-P. Zeolitic imidazolate framework-8 nanocrystal coated capillary for molecular sieving of branched alkanes from linear alkanes along with high-resolution chromatographic separation of linear alkanes. J. Am. Chem. Soc. 132, 13645–13647 (2010).
Chang, N. & Yan, X.-P. Exploring reverse shape selectivity and molecular sieving effect of metal-organic framework UIO-66 coated capillary column for gas chromatographic separation. J. Chromatogr. A 1257, 116–124 (2012).
Tao, Z.-R. et al. Untwisted restacking of two-dimensional metal-organic framework nanosheets for highly selective isomer separations. Nat. Commun. 10, 2911 (2019).
Tang, W.-Q. et al. Controlling the stacking modes of metal-organic framework nanosheets through host-guest noncovalent interactions. Angew. Chem. Int. Ed. Engl. 60, 6920–6925 (2021).
Natraj, A. et al. Single-crystalline imine-linked two-dimensional covalent organic frameworks separate benzene and cyclohexane efficiently. J. Am. Chem. Soc. 144, 19813–19824 (2022).
Yusuf, K. et al. Inverse gas chromatography demonstrates the crystallinity-dependent physicochemical properties of two-dimensional covalent organic framework stationary phases. Chem. Mater. 35, 1691–1701 (2023).
Meng, S.-S. et al. Enhancing separation abilities of “low-performance” metal-organic framework stationary phases through size control. Anal. Chem. 94, 14251–14256 (2022).
Acknowledgements
This work is supported by the National Natural Science Foundation of China (22174067, Z.-Y.G. and 22204078, M.X.), the Natural Science Foundation of Jiangsu Province of China (BK20220370, M.X.), Jiangsu Provincial Department of Education (22KJB150009, M.X.), the Priority Academic Program Development of Jiangsu Higher Education Institutions, State Key Laboratory of Analytical Chemistry for Life Science (SKLACLS2218, Z.-Y.G.), and the Postgraduate Research&Practice Innovation Program of Jiangsu Province (KYCX23_1684, S.-S.M.). This work is carried out with the support of Shanghai Synchrotron Radiation Facility Beamline BL17B1 (proposal 2021-NFPS-PT-006657).
Author information
Authors and Affiliations
Contributions
Z.-Y.G. conceived the idea and supervised the research. S.-S.M. and M.X. performed the synthesis, characterization, and GC experiments and discussed the results. H.-X.G. and X.-Q.K. performed the 2H SSNMR experiments. C.-L.C. and Y.H. performed the ultrahigh-resolution low-dose HRTEM imaging. P.-Y.C. assisted in revealing the structure of MOFs. B.D. and L.-G.X. assisted in the synthesis of deuterated H4TCPE-d16 ligands. Y.-H.G. assisted in analyzing the HAADF characterization. W.-Q.T. and W.-S.T. assisted in the GC experiments. S.Y. assisted in the DFT calculations. Z.-Y.G., S.-S.M., and M.X. discussed the experimental data and wrote the paper. All authors have approved the final version of the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks the anonymous reviewers for their contribution to the peer review of this work. A peer review file is available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Source data
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Meng, SS., Xu, M., Guan, H. et al. Anisotropic flexibility and rigidification in a TPE-based Zr-MOFs with scu topology. Nat Commun 14, 5347 (2023). https://doi.org/10.1038/s41467-023-41055-6
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-023-41055-6
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.