Abstract
Organic superconductors have π-molecular orbitals, from which electrons can become delocalized, giving rise to metallic conductivity due to orbital overlap between adjacent molecules. Here we report the discovery of superconductivity at a transition temperature (Tc) of ~5 K in alkali-metal-doped phenanthrene. A 1-GPa pressure leads to a 20% increase of Tc, suggesting that alkali-metal-doped phenanthrene shows unconventional superconductivity. Raman spectra indicate that alkali-metal doping injects charge into the system to realize the superconductivity. The discovery of superconductivity in A3phenanthrene (where A can be either K or Rb) produces a novel broad class of superconductors consisting of fused hydrocarbon benzene rings with π-electron networks. An increase of Tc with increasing number of benzene rings from three to five suggests that organic hydrocarbons with long chains of benzene rings are potential superconductors with high Tc.
Similar content being viewed by others
Introduction
Organic superconductors mainly belong to one of two families: the quasi-one-dimensional (TMTSF)2X and two-dimensional (BEDT–TTF)2X (refs 1,2), in which TMTSF is tetramethyltetraselenafulvalene (C10H12Se4), and BEDT–TTF is bis(ethylenedithio)tetrathiafulvalene (C10H8S8). The introduction of charge into C60 solids and graphites with π-electron networks by doping to realize superconductivity has been reported3,4. Organic superconductors exhibit many interesting phenomena, including low dimensionality, strong electron–electron and electron–phonon interactions and the proximity of antiferromagnetism, insulator states and superconductivity. They consist of open-shell molecular units that are the result of a partial oxidation and reduction of the donor and acceptor molecules in the crystal-growth process. The unpaired electrons residing in the π-molecular orbital of the donor unit are responsible for the electronic properties of these charge–transfer salts. π-Molecular orbitals also have an important role in the superconductivity of C60 solids and graphite superconductors. Key features of organic superconductors are the low dimensionality of the materials and a strong coupling of the charge carriers to the lattices. Organic superconductors provide a good system to study the interplay of strong electron–electron and electron–phonon interactions in low-dimensional system. It is striking that the close proximity of superconductivity to a magnetically ordered state occurs in organic superconductors5,6, similar to the other strongly correlated electron systems: the heavy fermion metals7 and high-temperature superconductors including cuprates8 and pnictides9,10. Therefore, it challenges the understanding of superconductivity. It is found that the Tc increases with the expansion of the lattice in alkali-metal-doped C60. This behaviour is expected by the Bardeen, Cooper and Schrieffer (BCS) theory, because the expansion of lattice leads to an enhancement of the density of states on the Fermi surface. However, the body-centered-cubic fulleride Cs3C60 is found to be a true Mott–Jahn–Teller insulator, and it possesses both the ingredients required by the strongly correlated theory11,12. The insulator Cs3C60 can be turned into superconductor by pressure13. The superconductivity induced by pressure in Cs3C60 is related to the antiferromagnetic Mott insulator11,12, similar to the cuprate. For the graphite superconductors with π-electron networks, C6Yb and C6Ca show superconductivity at 6.5 and 11.5 K (ref. 14), respectively. Such high transition temperatures are unprecedented although it is characterized by single-gap s-wave superconductivity15 and the coupling with intercalant phonon is believed to be main force for superconductivity16. Therefore, it indicates that superconductivity for the superconductors with π-electron networks is not simply explained by BCS theory. Recently, a potassium-doped picene (C22H14) with five fused benzene rings was shown to display superconductivity at a temperature as high as 18 K (ref. 17).
Here we report the discovery of superconductivity in alkali-metal-doped phenanthrene (C14H10). The work raises the prospect of producing a new family of superconductor based on aromatic hydrocarbons. The fact that Tc increases from 5 K for A3phenanthrene (A=K and Rb) with three benzene rings to 18 K for Kxpicene with five benzene rings suggests that organic hydrocarbons with long chains of benzene rings could be superconductors with high Tc. Our results indicate that such aromatic hydrocarbons may be unconventional superconductors.
Results
Crystal structure of phenanthrene and A3phenanthrene
The molecular structure and crystal structure of phenanthrene were shown in the inset of Figure 1a. Both phenanthrene and picene molecules are phenanthrene-like structure motif. The phenanthrene contains three fused benzene rings, whereas picene contains five. The ribbon-like molecular structure can be regarded as part of sheet of graphene. Figure 1a shows the X-ray diffraction pattern of phenanthrene. As shown in top panel, the phenanthrene crystallizes in P21 symmetry with lattice parameters: a=8.453 Å, b=6.175 Å, c=9.477 Å, β=98.28°. All peaks in X-ray diffraction pattern can be well indexed with the crystal structure mentioned above. Miller indices are marked in the pattern. The lattice constants obtained here are consistent with the results reported before18. The crystal that comprises layers stacked in c direction, where each layer (in a–b plane) contains phenanthrene molecules arranged in a herringbone structure, as shown in the inset of Figure 1a. Figure 1b shows the X-ray diffraction patterns of K3phenanthrene and Rb3phenanthrene with all reflections indexed with the P21 symmetry, and no impurity phase is observed for both K3phenanthrene and Rb3phenanthrene.
Figure 2 shows the X-ray diffraction pattern taken after exposing the superconducting K3phenanthrene to air for 5 min. As a comparison, the X-ray diffraction pattern for the as-grown K3phenanthrene is also displayed in Figure 2. As exposed to air, the black powder products changed to white quickly. But, it should be noted that no fierce reaction, such as combustion, can be observed as exposing the as-grown K3phenanthrene to air, suggesting that no elementary substance of potassium remains after the reaction of potassium and phenanthrene. Figure 2 shows that the diffraction peaks of KOH·H2O can obviously be observed, indicating that the de-intercalation of K3phenantrene occurs as exposed to air, and K reacts with water to form KOH·H2O. The potassium de-intercalating from K3phenantrene in air is consistent with the fact that the K3phenantrene loses the superconductivity quickly for exposing to air. Such instability of K3phenantrene in air is quite similar to that of alkali-metal-intercalated graphite19,20,21 and Kxpicene17.
With potassium intercalated into the phenanthrene, the lattice constants of K3phenantrene change to a=8.430 Å, b=6.134 Å, c=9.417 Å, β=98.18 ° and the unit cell volume contracts to 482.0 Å3 from 489.6 Å3. For Rb3phenanthrene, the lattice constants are a=8.450 Å, b=6.139 Å, c=9.442 Å, β=97.99° and the unit cell volume also contracts to 485.06 Å3 from 489.6 Å3. Such contraction of lattice parameters could arise from strong interaction between the benzene ring layers induced by K or Rb doping that leads to charge transfer from dopant to the benzene rings, which is confirmed by Raman spectra. The lattice parameters of the Rb3phenanthrene are slightly larger than that of the K3phenanthrene, which arises from the fact that the ionic radius of Rb is larger than that of K. The evolution of lattice constants with K doping is quite different from the case of Kxpicene reported by Mitsuhashi et al.17, in which the remarkable feature is that the lattice constants c and b shrink, whereas the a expands with intercalating K. This is also contrary to alkali-atoms-intercalated pentacene22, where the lattice constant of c axis is significantly expanded because of alkali metal atoms intercalating between the molecular layers of pentacene. The intercalations in the K3phenanthrene and Rb3phenanthrene are also quite different from (BEDT–TTF)2I3 (ref. 23) and (TMTSF)2PF6 (ref. 24) superconductors. In superconducting (BEDT–TTF)2I3 and (TMTSF)2PF6, the electron donor and acceptor layers form quasi-two-dimensional layers that is layer-by-layer stacked.
Susceptibility of A3phenanthrene
Figure 3a shows the magnetic susceptibility χ as a function of temperature for the powder samples of K3phenanthrene and Rb3phenanthrene in the zero-field cooling (ZFC) and field cooling (FC) measurement procedures under magnetic field H of 10Oe. The magnetic susceptibility χ versus T plot shows a sharp decrease below 4.95 K in ZFC and FC measurements for the K3phenanthrene, and here the temperature corresponding to the sharp decrease is defined as the superconducting transition temperature Tc. One can see that the superconducting transition is very sharp and transition width is less than 0.5 K. The diamagnetic χ in the ZFC measurements can be assigned to the shielding effect, and the shielding fraction is about 5.3%. As discussed by Mitsuhashi et al.17, the small shielding fraction in powder sample could arise from the penetration of magnetic field into superconducting phase because of smaller size of crystallites than the London penetration depth. When the K3phenanthren was pressed into a pellet, the shielding fraction is increased to 15.5%. The shielding fraction of the K3phenanthrene is larger than that of Kxpicene17. The fact that the shielding fraction can be increased when the powder sample was pressed to form a pellet suggests that the superconductivity is a bulk behaviour. The lower critical magnetic field HC1~175 Oe was estimated from the M versus H plot at 2.5 K (see inset of Figure 3a), less than HC1~380 Oe in K3.3picene with Tc~18 K at 5 K (ref. 17). As shown in Figure 3a, a superconducting transition at 4.75 K is observed in the susceptibility measured in ZFC and FC procedures for the powder sample Rb3phenanthrene with the shielding fraction of about 6.7%. It should be pointed out that Tc of Rb3phenanthrene is about 0.20 K less than that of K3phenanthrene. This is consistent with the case of picene in which the Tc is about 7.1 K for K doping, and shifts to 6.9 K for Rb doping. Figure 3b shows temperature dependence of χ under different magnetic fields for K3phenanthrene in the ZFC measurement. One can see that the diamagnetic signal disappears distinctly with increasing H, but there was an obvious drop of χ at 3.7 K even at 1,000 Oe. On the basis of data shown in Figure 3b, we obtained magnetic-field dependence of Tc, and plot the upper critical field HC2 versus T in the inset of Figure 3b.
The samples Kxphenanthrene with the nominal compositions (x=2.5, 2.8, 2.9, 3, 3.1, 3.2 and 3.5) were also synthesized in the same condition. It is found that only the sample with nominal composition K3phenanthrene shows superconductivity. To confirm it, we prepared five batches of samples of Kxphenanthrene for the each nominal composition with x=2.5, 2.8, 2.9, 3, 3.1, 3.2 and 3.5. The parameters of superconductivity for those Kxphenanthrene are displayed in Table 1, where Tc and shielding fractions were obtained from the magnetic susceptibility measurements. In the five batches of samples for each x, only the sample Kxphenanthrene with the nominal composition of x=3 shows superconducting transition. Although the superconducting fraction is quite different from batch to batch among the superconducting samples, the superconducting critical temperature Tc changes less than 5%. The difference of the superconducting fraction may arise from the different sizes of the crystallite. The shielding fraction from zero-field-cooled susceptibility is quite small, and the field-cooled susceptibility shows the small Meissner effect. These results could arise from the quite small size of crystallites for the powder samples, so that the penetration depth is much larger than the size of crystallites.
Effect of pressure on Tc for K3phenanthrene
Figure 4a presents the temperature-dependent magnetization for the powder sample Kxphenanthrene under the pressures ranging from ambient pressure to 1 GPa. The most notable result is that both Tc and shielding fraction increase rapidly with increasing the pressure. Tc is enhanced from 4.7 K at ambient pressure, to 5.9 K at 1 GPa. The pressure dependence of Tc is shown in Figure 4b. The positive d(Tc/Tc(0))/dP~0.26 GPa−1 at low pressure range (less than 1 GPa) in K3phenanthrene is similar to graphite intercalation compounds25. Such positive dependence would not be expected within a conventional weak coupling phonon model because Tc is usually suppressed by pressure for conventional superconductivity.
Raman spectra of phenanthrene and A3phenanthrene
Figure 5 shows the room-temperature Raman spectra for K3phenanthrene and Rb3phenanthrene as well as pure phenanthrene. There are seven major Raman peaks, which can be conveniently compared between pure and intercalated phenanthrene: 1,524, 1,441, 1,350, 1,037, 830, 411 and 250 cm−1, as listed in Table 2. All of these peaks belong to the A1 mode, and arise mainly from the C–C stretching vibration26,27. Compared with the pure phenanthrene, alkali-metal-doped phenanthrene displays obvious downshift, suggesting the phonon-mode softening effect. Such softening of the phonon modes should arise from the charge–transfer effect due to the intercalation of the alkali-metal into between phenanthrene molecules. Nominally, three electrons may transfer to a phenanthrene molecule for K3phenanthrene and Rb3phenanthrene. There are 17 and 21 cm−1 downshifts for the 1,441 cm−1 mode in K3phenanthrene (1424 cm−1) and Rb3phenanthrene (1,419 cm−1), respectively. It suggests 6 cm−1 per electron and 7 cm−1 per electron redshift with the complete transfer of charge. This is consistent with that observed in superconducting A3C60 (A=K, Rb)28, in which the redshift is also 6 cm−1 per electron for the mode at 1,460 cm−1. Theoretical calculations show that the C–C stretching A1 mode of 1,434 cm−1 (in monoanion of phenanthrene, 7 cm−1 downshift from 1441 cm−1 in the pure phenanthrene) strongly coupled to the a2 LUMO in phenanthrene and has large electron–phonon coupling constants in the monoanion of phenanthrene29. The linewidth of the modes are obviously increased in K- and Rb-doped samples. Similar behaviour has been observed in potassium-doped fullerides. Such a broadening of the modes arises from the electron–phonon interaction28. Kato et al. have studied the electron–phonon coupling and predicted occurrence of possible superconductivity in negatively charged phenanthrene-edge-type hydrocarbon crystals based on the BCS theory with strong electron–phonon coupling29. They found that the strength of electron–phonon coupling and Tcs have relevance to the molecular size and the molecular edge structures, and Tc and electron–phonon coupling constants decrease with increasing the molecular size.
Susceptibility of normal state for phenanthrene and A3phenanthrene
We measured the magnetic susceptibility of pure phenanthrene, and superconducting K3phenanthrene and Rb3phenanthrene, as shown in Figure 6. The magnetic susceptibilities in normal states for K3phenanthrene and Rb3phenanthrene are considerably large, and show the Curie–Weiss behaviour with the superconductivity completely suppressed under the magnetic field of 5 T. Pure phenanthrene shows diamagnetic behaviour, and the temperature-dependent negative magnetic susceptibility follows Curie–Weiss behaviour in the low-temperature regime. We fit the data of magnetic susceptibility with the formula χ=χ0+C/(T+θ), and the fitting results are listed in the Table 3. The values at 10 K for the alkali-intercalated phenanthrenes are much smaller than those reported in the superconducting Kxpiecene17. In the pure phenanthrene, only small magnetic moment of 0.06 μB per mole is obtained from the fitting, indicating that almost no local spin is present. While in the K3phenanthrene and Rb3phenanthrene, the magnetic moment increases to 0.22 μB per mole. It suggests that the charge transfer by the alkali intercalation into phenanthrene not only injects conduction electrons, but also induces local spins. This may hint an unconventional nature of the superconductivity in the alkali-metal-intercalated phenanthrene-edge-type hydrocarbons. Similar behaviour has been observed in Kxpicene. It implies that there exist local spins in these superconducting materials. It is well known that a positive pressure effect on superconductivity is widely observed in Cs3C60 (ref. 11), high-Tc cuprate compounds30 and iron-based superconductors31 as a consequence of the suppression of antiferromagnetism. Similar positive pressure effect on Tc in aromatic hydrocarbon superconductors may also be relevant to the suppression of the localized spin interaction by pressure.
Discussion
We prepared a series of Kxphenanthrene samples with different potassium content, and found that only the sample with nominal composition of K3phenanthrene shows superconductivity: all other samples with x deviation from 3 do not show superconductivity. We observed only a superconducting transition for the superconducting K3phenanthrene and Rb3phenanthrene; this is different from the case of potassium-doped picene in which there are two superconducting phases with Tc=7 and 18 K, respectively. There is a large family of polycyclic aromatic compounds with an extended phenanthrene-like structural motif designated as [n]phenacene, where n is the number of fused benzene rings. [n]Phenacene molecules are related to layers of graphene in the way that ribbons are related to sheets. Therefore, discovery of superconductivity in A3phenanthrene (A3C14H10, A=K and Rb) besides the superconductor Kxpicene opens a new broad family of superconductors that consists of aromatic hydrocarbons. To search for superconductors in such a family of [n]phenacene molecules and to study their physical properties is important to understand the mechanism of superconductivity. Tc of 5 K is relatively low for A3phenanthrene (A=K, Rb) with three benzene rings, compared with 7 and 18 K for Kxpicene with five benzene rings, suggesting that such organic hydrocarbons with long benzene rings are potential superconductors with high Tc.
A theoretical study by Kato et al.29 indicates that the electron–phonon coupling constants decrease with an increase in the number of carbon atoms in phenanthrene edge-type hydrocarbons. They estimated Tc for the hydrocarbon monoanions by using the approximate solution of the Eliashberg equation, and found that Tc decreases with increasing the number of carbon atoms in phenanthrene edge-type hydrocarbons. However, such theoretical prediction is in contrast to experimental results, which shows that Tc increases from ~5 to 7 K/18 K when increasing the number of benzene rings from 3 in phenanthrene to 5 in picene. It suggests that superconductivity in the phenanthrene edge-type hydrocarbons could be unconventional, and cannot be explained only by electron–phonon coupling. Enhancement of Tc with increasing pressure and coexistence of superconductivity and local spins are also the indications of unconventional superconductivity, because the existence of local spin destroys the superconductivity in the frame of BCS theory. Further evidence for unconventional superconductivity is the decrease of Tc by 0.2 K for Rb doped both phenanthrene and picene relative to K-doped samples, respectively, although the lattice constants slightly increase with change of dopant from K to Rb. This result is consistent with the pressure effect on Tc. This is totally different from the case of superconducting fullerides in which Tc increases with the expansion of the lattice in alkali-metal-doped C60 (ref. 32), which is expected by the BCS theory, because the expansion of lattice leads to an enhancement of the density of states at the Fermi level.
To confirm the proposed unconventional superconductivity, a high-quality superconducting sample, even a single crystal, may be required. This could allow the detailed determination of crystal and electronic structures and further investigation into the effects of pressure, and may reveal the mechanism of superconductivity in our organic hydrocarbon superconductors.
Methods
Phenanthrene purification and sample synthesis
The phenanthrene (from Alfa Aesar, 98% purity) was purified by sublimation method. The purchased phenanthrene was loaded at the bottom of a glass tube (diameter, 15 mm; length, 400 mm). The glass tube was sealed under vacuum of better than 5×10−4 Pa. One end of the tube, where the phenanthrene was located, was put at the middle of a tubular furnace, with a thermocouple attached. The other end of the glass tube was outside of the tubular furnace. The temperature was slowly raised to 85 °C and kept for one week. The purified phenanthrene was collected at the end that was kept outside the furnace during purification.
High-purity K metal (98%, Sinopharm Chemical Reagent) and phenanthrene purified by sublimation method were used as starting materials. The K metal was cut into small pieces (1 mm in diameter) and mixed with phenanthrene in the chemical stoichiometry, and then the mixture was loaded into a quartz tube (Φ=10 mm). The quartz tube was sealed under high vacuum of 1×10−4 Pa, and then heated to 200 °C in 40 min and kept at 200 °C for 24 h. For Rbxphenanthrene samples, the mixture of Rb metal and purified phenanthrene was heated from room temperature to 240 °C in 100 min, and kept at this temperature for 7 days. At 200 °C, both phenanthrene (melting point 101 °C) and potassium (melting point 63.65 °C) are in liquid state, which can speed up the chemical reaction and insure the homogeneity of the sample. The resulting Axphenanthrene (A=K and Rb) powder sample shows uniform dark black colour, which is totally different from the pure white colour of phenanthrene. The appearance of samples before and after annealing was shown as the inset of Figure 1b. In the Table 1, all samples of Kxphenanthrene are obtained by reacting the purified phenanthrene by sublimation method with K. The impurity phase of KH can be observed in X-ray diffraction pattern for the samples prepared by reacting the phenanthrene purchased from company with K. Axphenanthrene is quite sensitive to oxygen and moisture, and it will be decomposed in air within few minutes. All the processes except for annealing were done in glove box with the oxygen and moisture level less than 1 p.p.m.
Characterization of structure and susceptibility
Before the X-ray diffraction measurement, the samples were first ground into fine powder in a glove box, and then loaded into the capillaries (purchased from Hilgenberg GmbH, made of special glass no. 10. L=80 mm, OD=0.70 mm, Wall=0.01 mm); finally, the capillary was sealed to keep the sample in an inert atmosphere during X-ray diffraction measurement. The capillaries were fixed to the sample shelf of X-ray diffractometer (TTR-III theta/theta rotating anode X-ray Diffractometer) by plasticine. X-ray diffraction pattern was obtained in the 2-theta range of 5°–65° with a scanning rate of 0.5° per minute. The magnetization measurement was made by SQUID MPMS (Quantum Design). The sample was placed into Polypropylene powder holder (Quantum Design).
Susceptibility under pressure
The magnetization under pressure was measured by incorporating a copper–beryllium pressure cell (EasyLab) into SQUID MPMS (Quantum Design). The sample was firstly placed in a teflon cell (EasyLab) with coal oil (EasyLab) as the pressure media. Then, the teflon cell was set in the copper–beryllium pressure cell for magnetization measurement. The contribution of background magnetization against the sample at 2 K was less than 5%.
Raman spectrum
Raman-scattering experiments were carried out using the 780-nm laser line in DXR Raman Microscope (Thermo Scientific). The scattering light was captured with a single exposure of the CCD with a spectral resolution of 1 cm−1. The powder samples were loaded in the sealed capillary with highly pure Ar gas during Raman measurements. It should be pointed out that the X-ray diffraction and Raman measurements were carried out on the powder samples in the same capillary.
Additional information
How to cite this article: Wang, X.F. et al. Superconductivity at 5 K in alkali-metal-doped phenanthrene. Nat. Commun. 2:507 doi: 10.1038/ncomms1513 (2011).
References
Ishiguro, T., Yamaji, K. & Saito, G. in Organic Superconductors, 2nd edn (Springer-Verlag, 1997).
Singleton, J. Studies of quasi-two-dimensional organic conductors based on BEDT-TTF using high magnetic fields. Rep. Prog. Phys. 63, 1111–1207 (2000).
Hebbard, A. F. et al. Superconductivity at 18 K in potassium-doped C60 . Nature 350, 600–601 (1991).
Emery, N. et al. Superconductivity of bulk CaC6 . Phys. Rev. Lett. 95, 087003 (2005).
Kobayashi, H. et al. New BETS conductors with magnetic anions (BETS=bis(ethylenedithio) tetraselenafulvalene). J. Am. Chem. Soc. 118, 368–377 (1996).
Brossard, L. et al. Interlayer between chains of S=5/2 localised spins and two-dimensional sheets of organic donors in the synthetically built magnetic multilayer λ-(BETS)2FeCl4 . Eur. Phys. J. B 1, 439–452 (1998).
Mather, N. D. et al. Magnetically mediated superconductivity in heavy fermion compounds. Nature 394, 39–43 (1998).
Lee, P. A., Nagaosa, N. & Wen, X. G. Doping a Mott insulator: Physics in high-temperature superconductivity. Rev. Mod. Phys. 78, 17–84 (2006).
Drew, A. J. et al. Coexistence of static magnetism and superconductivity in SmFeAsO1−xFx as revealed by muon spin rotation. Nature Mater. 8, 310–314 (2009).
Chen, H. et al. Coexistence of the spin-density-wave and superconductivity in the (Ba, K)Fe2As2 85, 17006 (2009).
Takabayashi, Y. et al. The disorder-free non-BCS superconductor Cs3C60 emerges from an antiferromagnetic insulator parent state. Science 323, 1585–1590 (2009).
Durand, P. et al. The Mott-Hubbard insulating state and orbital degeneracy in the superconducting C603− fulleride family. Nature Mater. 2, 605–610 (2003).
Ganin, A. Y. et al. Bulk superconductivity at 38 K in a molecular system. Nature Mater. 7, 367–371 (2008).
Weller, T. E. et al. Superconductivity in the intercalated graphite compounds C6Yb and C6Ca.. Nature Phys. 1, 39–41 (2005).
Sutherland, M. et al. Bulk evidence for single-gap s-wave superconductivity in the intercalant graphite superconductor C6Yb. Phys. Rev. Lett. 98, 067003 (2007).
Mazin, I. I. Intercalant-driven superconductivity in YbC6 and CaC6 . Phys. Rev. Lett. 95, 227001 (2005).
Mitsuhashi, R. et al. Superconductivity in alkali-metal-doped picene. Nature 464, 76–79 (2010).
Trotter, J. et al. The crystal and molecular structure of phenanthrene. Acta. Cryst. 16, 605–608 (1963).
Matsumoto, R. et al. Thermal decomposition of cesium-ethylene-ternary graphite intercalation compounds. Thermochim. Acta 507–508, 142–145 (2010).
Bindra, C. et al. Super dense LiC2 as a high capacity Li intercalation anode. J. Electrochem. Soc. 145, 2377 (1998).
Baumann, J. A. et al. Graphite intercalated alkali metal vapour sources. European Patent Application Number:84304410.8.
Minakata, T. et al. Conducting thin films of pentacene doped with alkaline metals. J. Appl. Phys. 74, 1079 (1993).
Madsen, D. et al. The single crystal structure of the organic superconductor βco-(BEDT-TTF)2I3 from a powder grain. Acta Cryst. B55, 601–606 (1999).
Han, Y. K. et al. Fabrication of (TMTSF)2PF6 thin crystals in a confined electrode. Synthetic Metals 157, 492–496 (2007).
Kim, J. S. et al. Effect of pressure on superconducting Ca-intercalated graphite CaC6 . Phys. Rev. B 74, 214513 (2006).
Martin, J. M. L. et al. Structure and vibrational spectrum of some polycyclic aromatic compounds studied by density function theory :1: Naphthalene, Azulene, Phenanthrene and Authracene. J. Phys. Chem. 100, 15358–15367 (1996).
Godec, J. & Colombo, L. Interpretation of the vibration spectrum of crystalline phenanthrene. J. Chem. Phys. 65, 4693 (1976).
Zhou, P. et al. Raman scattering in C60 and alkali-metal-saturated C60 . Phys. Rev. B 46, 2595–2605 (1992).
Kato, T., Yoshizawa, K. & Hirao, K. Electron–phonon coupling in negatively charged acene- and phenanthrene-edge-type hydrocarbon crystals. J. Chem. Phys. 116, 3420 (2002).
Gao, L. et al. Superconductivity up to 164 K in HgBa2Cam−1CumO2m+2+δ (m=1, 2, and 3) under quasi-hydrostatic pressures. Phys. Rev. B 50, 4260–4263 (1994).
Takahashi, H. et al. Superconductivity at 43 K in an iron-based layered compound LaO1−xFxFeAs. Nature 453, 376–378 (2008).
Fleming, R. M. et al. Relation of structure and superconducting transition temperatures in A3C60 . Nature 352, 787–788 (1991).
Bandyopadhyay, I. & Manogaran, S. Force field and assignement of the vibrational spectra of phenanthrene—an ab initio study. J. Mol. Struct. Theochem 496, 107 (2006).
Acknowledgements
We thank Dr Z. Sun for useful discussion and for improving language of the manuscript. We also thank Professor F. K. Chen for providing the Raman system, and S. Q. Li for his help in Raman measurements. This work was supported by the Natural Science Foundation of China, and by National Basic Research Program of China and Chinese Academy of Sciences.
Author information
Authors and Affiliations
Contributions
X.H.C. designed and coordinated the whole experiment, analysed the data and wrote the paper. X.F.W. performed the synthesis, and X-ray diffraction and magnetization measurements. R.H.L. carried out the structural analysis and analysed the data. X.F.W. and X.G.L. run Raman measurements. Z.G., Y.L.X., Y.J.Y., J.J.Y. and X.G.L. contributed to some of the magnetization and high-pressure measurements.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
About this article
Cite this article
Wang, X., Liu, R., Gui, Z. et al. Superconductivity at 5 K in alkali-metal-doped phenanthrene. Nat Commun 2, 507 (2011). https://doi.org/10.1038/ncomms1513
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms1513
This article is cited by
-
Structure, charge transfer, and superconductivity of M-doped phenanthrene (M = Al, Ga, and In): A comparative study of K-doped cases
Science China Physics, Mechanics & Astronomy (2019)
-
Electronic and optical responses of quasi-one-dimensional phosphorene nanoribbons to strain and electric field
Scientific Reports (2018)
-
π-electron S = ½ quantum spin-liquid state in an ionic polyaromatic hydrocarbon
Nature Chemistry (2017)
-
Redox-controlled potassium intercalation into two polyaromatic hydrocarbon solids
Nature Chemistry (2017)
-
Synthesis successes
Nature Chemistry (2017)